Exterior material for power storage device, method for manufacturing same, and power storage device

ABSTRACT

This exterior material for a power storage device is configured from a laminate comprising at least a surface coating layer, a base layer, a barrier layer, and a heat sealing resin layer in order from the outside, and moreover is such that a logarithmic decrement ΔE at 60° C. in a rigid body pendulum measurement of the outside surface of the surface coating layer of the laminate is 0.12 or less.

TECHNICAL FIELD

The present disclosure relates to an exterior material for electrical storage devices, a method for manufacturing the exterior material for electrical storage devices, and an electrical storage device.

BACKGROUND ART

Various types of electrical storage devices have been developed heretofore, and in every electrical storage device, an exterior material is an essential member for sealing electrical storage device elements such as an electrode and an electrolyte. Metallic exterior materials have been often used heretofore as exterior materials for electrical storage devices.

On the other hand, in recent years, electrical storage devices have been required to be diversified in shape and to be thinned and lightened with improvement of performance of electric cars, hybrid electric cars, personal computers, cameras, mobile phones and so on. However, metallic exterior material for electrical storage devices that have often been heretofore used have the disadvantage that it is difficult to keep up with diversification in shape, and there is a limit on weight reduction.

Thus, in recent years, a film-shaped laminate with a base material layer, a barrier layer, and a heat-sealable resin layer laminated in this order has been proposed as an exterior material for electrical storage devices which is easily processed into diversified shapes and is capable of achieving thickness reduction and weight reduction (see, for example, Patent Document 1).

In such an exterior material for electrical storage devices, generally, a concave portion is formed by cold molding, electrical storage device elements such as an electrode and an electrolytic solution are disposed in a space formed by the concave portion, and heat-sealable resin layers are heat-sealed (thermally sealed) to obtain an electrical storage device with electrical storage device elements stored in the exterior material for electrical storage devices.

PRIOR ART DOCUMENT Patent Document

-   Patent Document 1: Japanese Patent Laid-open Publication No.     2008-287971

SUMMARY OF THE INVENTION Problems to be Solved by the Invention

In an exterior material for electrical storage devices which includes a film-shaped laminate, a surface coating layer may be provided outside a base material layer for the purpose of, for example, protecting the base material layer and imparting designability.

The electrical storage device is fixed to housings of various products with a pressure sensitive adhesive tape (double-sided pressure sensitive adhesive tape) or the like interposed therebetween. A surface of the electrical storage device (i.e. a surface of the exterior material for electrical storage devices) and the pressure sensitive adhesive tape are brought into close contact with each other to fix the electrical storage device to the housing. Thus, the outer surface of the exterior material for electrical storage devices which forms the surface of the electrical storage device is required to have high adhesion to the pressure sensitive adhesive tape. In particular, the exterior material for electrical storage devices in, for example, an electric car, a hybrid electric car, a personal computer, a camera or a mobile phone, and the outer surface of the exterior material for electrical storage devices is also required to have high adhesion to the pressure sensitive adhesive tape in a high-temperature environment (e.g. about 60° C.).

Under these circumstances, a main object of a first embodiment of the present disclosure is to provide an exterior material for electrical storage devices which includes a surface coating layer on an outer surface, in which the surface coating layer forming the outer surface has high adhesion to a pressure sensitive adhesive tape in a high-temperature environment.

In the process of manufacturing an electrical storage device, an electrical storage device element such as an electrolyte is put in a packaging formed of a molded exterior material for electrical storage devices, and baking treatment is then performed in a high-temperature environment (e.g. about 80 to 120° C.) for the purpose of, for example, making the electrical storage device element adaptive.

From the viewpoint of, for example, productivity (e.g. restriction of space for baking treatment), the baking step is carried out with electrical storage devices stacked on one on top of another. For this reason, there is a problem that in a high-temperature environment, electrical storage devices are transported and stacked, and at this time, the electrical storage devices are impacted, and easily damaged, for example, the electrical storage devices have an impaired shape, or are streaked or scraped.

Under these circumstances, a main object of a second embodiment of the present disclosure is to provide an exterior material for electrical storage devices which is hardly damaged in a high-temperature environment.

Means for Solving the Problem

The inventors of the present disclosure have extensively conducted studies for solving the above-described problems of the first embodiment. As a result, it has been found that an exterior material for electrical storage devices which includes a laminate including at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in this order from the outside and in which the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate is 0.120 or less at 60° C. in measurement with a rigid body pendulum has high adhesion to a pressure sensitive adhesive tape.

The first embodiment of the present disclosure has been completed by further conducting studies based on the above-mentioned findings. That is, the first embodiment of the present disclosure provides an invention of an aspect as described below.

This exterior material for electrical storage devices is configured from a laminate comprising at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in order from the outside, and moreover is such that a logarithmic decrement ΔE at 60° C. in a rigid body pendulum measurement of the outside surface of the surface coating layer of the laminate is 0.120 or less.

The inventors of the present disclosure have extensively conducted studies for solving the above-described problems of the second embodiment. As a result, it has been found that an exterior material for electrical storage devices which includes a laminate including at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in this order from the outside and in which the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate is 0.200 or less at 110° C. in measurement with a rigid body pendulum is hardly damaged in high-temperature environment (110° C.).

The second embodiment of the present disclosure has been completed by further conducting studies based on the above-mentioned findings. That is, the second embodiment of the present disclosure provides an invention of an aspect as described below.

This exterior material for electrical storage devices is configured from a laminate comprising at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in order from the outside, and moreover is such that a logarithmic decrement ΔE at 110° C. in a rigid body pendulum measurement of the outside surface of the surface coating layer of the laminate is 0.200 or less.

Advantages of the Invention

According to the first embodiment of the present disclosure, it is possible to provide an exterior material for electrical storage devices which includes a surface coating layer on an outer surface, in which the surface coating layer forming the outer surface has high adhesion to a pressure sensitive adhesive tape in a high-temperature environment (e.g. about 60° C.). According to the first embodiment of the present disclosure, it is also possible to provide a method for manufacturing the exterior material for electrical storage devices, and an electrical storage device obtained using the exterior material for electrical storage devices.

According to the second embodiment of the present disclosure, it is possible is to provide an exterior material for electrical storage devices which is hardly damaged in a high-temperature environment. According to the second embodiment of the present disclosure, it is also possible to provide a method for manufacturing the exterior material for electrical storage devices, and an electrical storage device obtained using the exterior material for electrical storage devices.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic diagram showing an example of a cross-sectional structure of an exterior material for electrical storage devices according to the present disclosure.

FIG. 2 is a schematic diagram showing an example of a cross-sectional structure of an exterior material for electrical storage devices according to the present disclosure.

FIG. 3 is a schematic diagram showing an example of a cross-sectional structure of an exterior material for electrical storage devices according to the present disclosure.

FIG. 4 is a schematic diagram for illustrating a method for housing an electrical storage device element in a packaging formed from an exterior material for electrical storage devices according to the present disclosure.

FIG. 5 is a schematic diagram for illustrating a method for measuring a logarithmic decrement ΔE in measurement with a rigid pendulum.

FIG. 6 is a schematic diagram for illustrating a method for evaluation of tape adhesion.

FIG. 7 is a schematic diagram for illustrating a method for evaluation of tape adhesion.

EMBODIMENTS OF THE INVENTION

An exterior material for electrical storage devices according to the first embodiment of the present disclosure includes a laminate including at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in this order from the outside, and the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate is 0.120 or less at 60° C. in measurement with a rigid body pendulum. The exterior material for electrical storage devices according to the first embodiment of the present disclosure has such a configuration, so that the surface coating layer forming the outer surface can exhibit high adhesion to a pressure sensitive adhesive tape in a high-temperature environment (e.g. about 60° C.).

An exterior material for electrical storage devices according to the second embodiment of the present disclosure includes a laminate including at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in this order from the outside, and in the surface coating layer, the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate is 0.200 or less at 110° C. in measurement with a rigid body pendulum. The exterior material for electrical storage devices according to the first embodiment of the present disclosure has such a configuration, and thus is hardly damaged in a high-temperature environment.

Hereinafter, the exterior material for electrical storage devices according to the present disclosure will be described in detail. In the present specification, matters specific to the first embodiment and the second embodiment of the present disclosure are specified as matters related to the respective embodiments, matters common to the first embodiment and the second embodiment are described in the present disclosure without being particularly specified, and redundant description is appropriately omitted. In the present specification, a numerical range indicated by the term “A to B” means “A or more” and “B or less”. For example, the expression of “2 to 15 mm” means 2 mm or more and 15 mm or less.

1. Laminated Structure and Physical Property of Exterior Material for Electrical Storage Devices

As shown in, for example, FIGS. 1 to 3 , an exterior material 10 for electrical storage devices according to the present disclosure includes a laminate including at least a surface coating layer 6, a base material layer 1, a barrier layer 3 and a heat-sealable resin layer 4 in this order from the outside. In the exterior material 10 for electrical storage devices, the surface coating layer 6 is an outermost layer, and the heat-sealable resin layer 4 is an innermost layer. In construction of the electrical storage device using the exterior material 10 for electrical storage devices and electrical storage device elements, the electrical storage device elements are put in a space formed by heat-sealing the peripheral portions of heat-sealable resin layers 4 of the exterior material 10 for electrical storage devices which face each other. In the laminate forming the exterior material 10 for electrical storage devices according to the present disclosure, the heat-sealable resin layer 4 is on the inner side with respect to the barrier layer 3, and the surface coating layer 6 is on the outer side with respect to the barrier layer 3.

In the present disclosure, as shown in, for example, FIGS. 2 and 3 , the exterior material 10 for electrical storage devices may have an adhesive agent layer 2 between the base material layer 1 and the barrier layer 3 if necessary for the purpose of, for example, improving bondability between these layers. A colored layer may be provided between the base material layer 1 and the barrier layer 3 (not shown). As shown in, for example, FIG. 3 , an adhesive layer 5 may be present between the barrier layer 3 and the heat-sealable resin layer 4 if necessary for the purpose of, for example, improving bondability between these layers.

In the present disclosure, the thickness of the laminate forming the exterior material 10 for electrical storage devices is not particularly limited, and the upper limit thereof is preferably about 190 μm or less, about 180 μm or less, or about 160 μm or less, about 155 μm or less, about 140 μm or less, about 130 μm or less, or about 120 μm or less, from the viewpoint of cost reduction, energy density improvement, and the like. The thickness of the laminate forming the exterior material 10 for electrical storage devices is preferably about 35 μm or more, about 45 μm or more, about 60 μm or more, about 75 μm or more, or about 80 μm or more, from the viewpoint of maintaining the function of an exterior material for electrical storage devices, which is protection of an electrical storage device element. The thickness of the laminate forming the exterior material 10 for electrical storage devices is preferably in the range of, for example, about 35 to 190 μm, about 35 to 180 μm, about 35 to 160 μm, about 35 to 155 μm, about 35 to 140 μm, about 35 to 130 μm, about 35 to 120 μm, about 45 to 190 μm, about 45 to 180 μm, about 45 to 160 μm, about 45 to 155 μm, about 45 to 140 μm, about 45 to 130 μm, about 45 to 120 μm, about 60 to 190 μm, about 60 to 180 μm, about 60 to 160 μm, about 60 to 155 μm, about 60 to 140 μm, about 60 to 130 μm, about 60 to 120 μm, about 75 to 190 μm, about 75 to 180 μm, about 75 to 160 μm, about 75 to 155 μm, about 75 to 140 μm, about 75 to 130 μm, about 75 to 120 μm, about 80 to 190 μm, about 80 to 180 μm, about 80 to 160 μm, about 80 to 155 μm, about 80 to 140 μm, about 80 to 130 μm, and about 80 to 120 μm. Above all, the thickness is particularly preferably about 80 to 130 μm.

In the exterior material 10 for electrical storage devices according to the present disclosure, the ratio of the total thickness of the surface coating layer 6, the base material layer 1, the adhesive agent layer 2 provided if necessary, the barrier layer 3, the adhesive layer 5 provided if necessary, and the heat-sealable resin layer 4 to the thickness (total thickness) of the laminate forming the exterior material 10 for electrical storage devices is preferably 90% or more, more preferably 95% or more, still more preferably 98% or more. As a specific example, when the exterior material 10 for electrical storage devices according to the present disclosure includes the surface coating layer 6, the base material layer 1, the adhesive agent layer 2, the barrier layer 3, the adhesive layer 5 and the heat-sealable resin layer 4, the ratio of the total thickness of these layers to the thickness (total thickness) of the laminate forming the exterior material 10 for electrical storage devices is preferably 90% or more, more preferably 95% or more, still more preferably 98% or more. In addition, when the exterior material 10 for electrical storage devices according to the present disclosure is a laminate including the surface coating layer 6, the base material layer 1, the adhesive agent layer 2, the barrier layer 3 and the heat-sealable resin layer 4, the ratio of the total thickness of these layers to the thickness (total thickness) of the laminate forming the exterior material 10 for electrical storage devices may be, for example, 80% or more, preferably 90% or more, more preferably 95% or more, still more preferably 98% or more.

In the exterior material 10 for electrical storage devices according to the first embodiment of the present disclosure, the logarithmic decrement ΔE of the outer surface of the surface coating layer 6 of the laminate forming the exterior material 10 for electrical storage devices is 0.120 or less at 60° C. in measurement with a rigid body pendulum. The exterior material 10 for electrical storage devices according to the first embodiment has the above-described logarithmic decrement ΔE at a high temperature of 60° C., so that the high adhesion of the surface coating layer 6 to the pressure sensitive adhesive tape in a high-temperature environment is secured. More specifically, in the exterior material for electrical storage devices according to the first embodiment, the surface coating layer may have a property of being very hard in a high-temperature environment at 60° C. because the logarithmic decrement ΔE of the surface coating layer at 60° C. is set to a very small value of 0.120 or less. For this reason, it is considered that in the case where a force of peeling the pressure sensitive adhesive tape attached to the surface coating layer from the surface coating layer is applied, the surface coating layer hardly moves, and thus high adhesion is exhibited. A surface of the electrical storage device (i.e. the outer surface of the exterior material for electrical storage devices) and the pressure sensitive adhesive tape are brought into close contact with each other to fix the electrical storage device to the housing.

In the first embodiment, the logarithmic decrement ΔE of the surface coating layer 6 at 60° C. may be 0.120 or less, and from the viewpoint of more suitably exhibiting high adhesion of the surface coating layer 6 to the pressure sensitive adhesive tape in a high-temperature environment, the logarithmic decrement ΔE is preferably about 0.100 or less, more preferably about 0.085 or less, still more preferably 0.080 or less. From the same viewpoint, the logarithmic decrement ΔE of the surface coating layer 6 at 60° C. is preferably about 0.030 or more, more preferably about 0.050 or more, still more preferably about 0.060 or more. The logarithmic decrement ΔE of the surface coating layer 6 at 60° C. is preferably in the range of about 0.030 to 0.120, about 0.030 to 0.100, about 0.030 to 0.085, about 0.030 to 0.080, about 0.050 to 0.120, about 0.050 to 0.100, about 0.050 to 0.085, about 0.050 to 0.080, about 0.060 to 0.120, about 0.060 to 0.100, about 0.060 to 0.085, or about 0.060 to 0.080. Above all, the logarithmic decrement ΔE is particularly preferably about 0.050 to 0.080 or about 0.060 to 0.080.

In the first embodiment, the logarithmic decrement ΔE of the surface coating layer 6 at 30° C. is preferably 0.080 or less, more preferably 0.070 or less, still more preferably 0.060 or less, from the viewpoint of suitably exhibiting high adhesion of the surface coating layer 6 to the pressure sensitive adhesive tape in a room temperature environment. From the same viewpoint, the logarithmic decrement ΔE of the surface coating layer 6 at 30° C. is preferably about 0.030 or more, more preferably about 0.040 or more, still more preferably about 0.046 or more. The logarithmic decrement ΔE of the surface coating layer 6 at 30° C. is preferably in the range of about 0.030 to 0.080, about 0.030 to 0.070, about 0.030 to 0.060, about 0.040 to 0.080, about 0.040 to 0.070, about 0.040 to 0.060, about 0.046 to 0.080, about 0.046 to 0.070, or about 0.046 to 0.060. In the first embodiment, the logarithmic decrement ΔE at 60° C. or 30° C. is measured as follows.

[Measurement of Logarithmic Decrement ΔE of Outer Surface of Surface Coating Layer in First Embodiment]

The exterior material for electrical storage devices is cut into a rectangle having a width of 15 mm (TD: Transverse Direction) and a length of 100 mm (MD: Machine Direction). Next, the heat-sealable resin layer is peeled from the barrier layer. When an adhesive layer is present between the heat-sealable resin layer and the barrier layer, the adhesive layer is also peeled from the barrier layer. Specifically, at 20 mm from the end in the length direction, a cut is made which extends from the surface coating layer side to the barrier layer. Pulling is performed from the left and the right with the cut at the center, so that the cut in the surface coating layer and the barrier layer is expanded to achieve cutting, and the heat-sealable resin layer (and adhesive layer) is stretched. At the time when the heat-sealable resin layer (adhesive layer) is stretched, the heat-sealable resin layer (and adhesive layer) is peeled from the barrier layer. The exterior material for electrical storage devices in which the heat-sealable resin layer (and adhesive layer) is peeled is cut into a rectangle having a width of 15 mm (TD) and a length of 50 mm (MD: Machine Direction) to obtain a test sample S. As shown in FIG. 5 , a rigid body pendulum physical property tester (model: RPT-3000W manufactured by A&D Company, Limited) is used, FRB-100 is used for a frame of a pendulum 30, cylindrical cylinder edge 30 a (RBP-080) is used for the edge portion, and the initial amplitude is set to about 0.3 degrees. The pendulum 30 is placed in such a manner that the central axis direction of the cylindrical cylinder and the machine direction of the test sample S are orthogonal to each other. In addition, for preventing floating and warpage of the test sample S during measurement, a kapton tape is attached to the test sample S at a position having no effect on measurement results, and fixed. The cylindrical cylinder edge 30 a is brought into contact with the outer surface of the surface coating layer. Next, the logarithmic decrement ΔE of the surface coating layer is measured in a temperature range of 30° C. to 200° C. at a temperature rise rate of 3° C./min using a cold block 31 (CHB-100). The temperature may be raised to 90° C. or higher, and is not required to be raised to 200° C. A logarithmic decrement ΔE is adopted at which the temperature of the surface coating layer of the test sample S is 60° C. or 30° C. An average of two measurements (N=2) made by using an unused cut sample rather than using a test sample once measured is used. When only an exterior material for electrical storage devices which has a size smaller than that of the test sample having the above-described size can be provided, a test sample having a size in a measurable range is provided and the measurement is performed. Even when MD and TD of the test sample cannot be identified, the measurement is performed with a test sample provided without identifying the direction because MD and TD do not have a significant effect on measurement results. When an exterior material for electrical storage devices is obtained from an electrical storage device and a test sample is provided, the exterior material for electrical storage devices is obtained from a portion on which molding has little effect, such as a top surface or a side surface of the electrical storage device.

In the first embodiment, the logarithmic decrement ΔE at 60° C. and the logarithmic decrement ΔE at 30° C. can be each adjusted by the composition (types and contents of resin, filler and the like) of the resin composition forming the surface coating layer 6, curing conditions, the molecular weight, the number of functional groups, the crosslinking density, the bulkiness of substituents, and the like.

In the exterior material 10 for electrical storage devices according to the second embodiment, the logarithmic decrement ΔE of the outer surface of the surface coating layer 6 of the laminate forming the exterior material 10 for electrical storage devices is 0.200 or less at 110° C. in measurement with a rigid body pendulum. The exterior material 10 for electrical storage devices according to the second embodiment has the above-described logarithmic decrement ΔE at a high-temperature environment at 110° C., and thus the exterior material for electrical storage devices is hardly damaged in a high-temperature environment.

In the second embodiment, the logarithmic decrement ΔE at 110° C. may be 0.200 or less, and from the viewpoint of more suitably enhancing damage resistance in a high-temperature environment, the logarithmic decrement ΔE is preferably about 0.180 or less, more preferably about 0.160 or less, still more preferably 0.145 or less, and preferably about 0.100 or more, more preferably about 0.120 or more, and is preferably in the range of about 0.100 to 0.200, about 0.100 to 0.180, about 0.100 to 0.160, about 0.100 to 0.145, about 0.120 to 0.200, about 0.120 to 0.180, about 0.120 to 0.160, or about 0.120 to 0.145. Above all, the logarithmic decrement ΔE is particularly preferably about 0.120 to 0.160.

In the second embodiment, from the viewpoint of enhancing damage resistance in a room temperature environment in addition to damage resistance in a high-temperature environment, the logarithmic decrement ΔE at 30° C. in rigid body pendulum measurement of the outer surface of the surface coating layer 6 of the laminate forming the exterior material for electrical storage devices according to the second embodiment is preferably about 0.080 or less, more preferably about 0.060 or less, and preferably about 0.020 or more, more preferably about 0.030 or more, and is preferably in the range of about 0.020 to 0.080, about 0.020 to 0.060, about 0.030 to 0.080, and about 0.030 to 0.060. Above all, the logarithmic decrement ΔE is particularly preferably about 0.030 to 0.060.

In the second embodiment, the logarithmic decrement ΔE at 110° C. or 30° C. is measured as follows.

[Measurement of Logarithmic Decrement ΔE of Outer Surface of Surface Coating Layer in Second Embodiment]

The exterior material for electrical storage devices is cut into a rectangle having a width of 15 mm (TD: Transverse Direction) and a length of 100 mm (MD: Machine Direction). Next, the heat-sealable resin layer is peeled from the barrier layer. When an adhesive layer is present between the heat-sealable resin layer and the barrier layer, the adhesive layer is also peeled from the barrier layer. Specifically, at 20 mm from the end in the length direction, a cut is made which extends from the surface coating layer side to the barrier layer. Pulling is performed from the left and the right with the cut at the center, so that the cut in the surface coating layer and the barrier layer is expanded to achieve cutting, and the heat-sealable resin layer (and adhesive layer) is stretched. At the time when the heat-sealable resin layer (adhesive layer) is stretched, the heat-sealable resin layer (and adhesive layer) is peeled from the barrier layer. The exterior material for electrical storage devices in which the heat-sealable resin layer (and adhesive layer) is peeled is cut into a rectangle having a width of 15 mm (TD) and a length of 50 mm (MD: Machine Direction) to obtain a test sample S (FIG. 5 ). The purpose of peeling the heat-sealable resin layer (and adhesive layer) from the barrier layer to obtain a sample (sample including a surface coating layer, a base material layer and a barrier layer) of the exterior material for electrical storage devices which is outside the barrier layer is elimination of the effect of the heat-sealable resin layer on measurement of the logarithmic decrement ΔE. As shown in FIG. 5 , a rigid body pendulum physical property tester (model: RPT-3000W manufactured by A&D Company, Limited) is used, FRB-100 is used for a frame of a pendulum 30, cylindrical cylinder edge 30 a (RBP-080) is used for the edge portion, and the initial amplitude is set to about 0.3 degrees. The pendulum 30 is placed in such a manner that the central axis direction of the cylindrical cylinder and the machine direction of the test sample S are orthogonal to each other. In addition, for preventing floating and warpage of the test sample S during measurement, a kapton tape is attached to the test sample S at a position having no effect on measurement results, and fixed. The cylindrical cylinder edge 30 a is brought into contact with the outer surface of the surface coating layer. Next, the logarithmic decrement ΔE of the surface coating layer is measured in a temperature range of 30° C. to 200° C. at a temperature rise rate of 3° C./min using a cold block 31 (CHB-100). The temperature may be raised to 110° C. or higher, and is not required to be raised to 200° C. A logarithmic decrement ΔE is adopted at which the temperature of the surface coating layer of the test sample S is 110° C. or 30° C. An average of two measurements (N=2) made by using an unused cut sample S rather than using the test sample S once measured is used. When only an exterior material for electrical storage devices which has a size smaller than that of the test sample S having the above-described size can be provided, the test sample S having a size in a measurable range is provided and the measurement is performed. Even when MD and TD of the test sample S cannot be identified, the measurement is performed with the test sample S provided without identifying the direction because MD and TD do not have a significant effect on measurement results. When an exterior material for electrical storage devices is obtained from an electrical storage device and the test sample S is provided, the exterior material for electrical storage devices is obtained from a portion on which molding has little effect, such as a top surface or a side surface of the electrical storage device.

In the second embodiment, the logarithmic decrement ΔE at 110° C. and the logarithmic decrement ΔE at 30° C. can be each adjusted by the composition (types and contents of resin, curing agent, filler and the like) of the resin composition forming the surface coating layer 6, curing conditions, the molecular weight, the number of functional groups, the crosslinking density, the bulkiness of substituents, and the like.

In the second embodiment, a resin having a property of being hard in a high-temperature environment is selected from commercially available resins as a resin for forming the surface coating layer 6, a resin composition for forming the surface coating layer 6 is prepared, the logarithmic decrement ΔE at 110° C. is measured, and a resin having a logarithmic decrement ΔE of 0.200 or less can be adopted for the surface coating layer 6.

Further, in the exterior material for electrical storage devices according to the second embodiment, the barrier layer 3 includes a stainless steel foil, and therefore the logarithmic decrement ΔE at 110° C. is more easily set to 0.200 or less as compared to a case where, for example, the barrier layer 3 is formed of an aluminum alloy foil. This may be because a stainless steel foil has a property of being harder as compared to an aluminum alloy foil.

From the viewpoint of imparting a matte-toned design to the outer surface of the exterior material 10 for electrical storage devices according to the present disclosure to a matte design, the arithmetic average roughness Rai of the outer surface of the surface coating layer 6 in the exterior material 10 for electrical storage devices according to the present disclosure is preferably about 0.10 μm or more, more preferably about 0.20 μm or more, still more preferably about 0.30 μm or more, even more preferably about 0.40 μm or more, even more preferably 0.50 or more, and preferably about 0.90 μm or less, more preferably about 0.80 μm or less, still more preferably about 0.70 μm or less, and is preferably in the range of about 0.10 to 0.90 μm, about 0.10 to 0.80 μm, about 0.10 to 0.70 μm, about 0.20 to 0.90 μm, about 0.20 to 0.80 μm, about 0.20 to 0.70 μm, about 0.30 to 0.90 μm, about 0.30 to 0.80 μm, about 0.30 to 0.70 μm, about 0.40 to 0.90 μm, about 0.40 to 0.80 μm, about 0.40 to 0.70 μm, about 0.50 to 0.90 μm, about 0.50 to 0.80 μm, or about 0.50 to 0.70 μm. Above all, the arithmetic average roughness is particularly preferably about 0.20 to 0.80 μm.

2. Layers Forming Exterior Material for Electrical Storage Devices [Surface Coating Layer 6]

The exterior material 10 for electrical storage devices according to the first embodiment includes a surface coating layer 6 on the base material layer 1 (on a side opposite to the barrier layer 3 from the base material layer 1) for the purpose of improving at least one of designability, electrolytic solution resistance, scratch resistance, moldability and the like. The exterior material 10 for electrical storage devices according to the second embodiment includes the surface coating layer 6 on the base material layer 1 (on the base material layer 1 on a side opposite to the barrier layer 3) for improvement of damage resistance in a high-temperature environment as one of purposes. In the present disclosure, the surface coating layer 6 is a layer located on the outermost layer of the exterior material 10 for electrical storage devices when the electrical storage device is constructed using the exterior material for electrical storage devices. That is, the surface coating layer 6 forms the outer surface of the exterior material 10 for electrical storage devices according to the present disclosure.

The resin contained in the resin composition forming the surface coating layer 6 in the first embodiment is not particularly limited as long as the logarithmic decrement ΔE is 0.120 or less at 60° C. As described above, in the first embodiment, the logarithmic decrement ΔE at 60° C. and the logarithmic decrement ΔE at 30° C. can be each adjusted by the composition (types and contents of resin, filler and the like) of the resin composition forming the surface coating layer 6, curing conditions, the molecular weight, the number of functional groups, the crosslinking density, the bulkiness of substituents, and the like. In the first embodiment, a resin having a property of being hard in a high-temperature environment is selected from commercially available resins as a resin for forming the surface coating layer 6, a resin composition for forming the surface coating layer 6 is prepared, the logarithmic decrement ΔE at 60° C. is measured, and a resin having a logarithmic decrement ΔE of 0.120 or less can be adopted for the surface coating layer 6.

The resin contained in the resin composition forming the surface coating layer 6 in the second embodiment is not particularly limited as long as the logarithmic decrement ΔE is 0.200 or less at 110° C. As described above, in the second embodiment, the logarithmic decrement ΔE at 110° C. and the logarithmic decrement ΔE at 30° C. can be each adjusted by the composition (types and contents of resin, curing agent, filler and the like) of the resin composition forming the surface coating layer 6, curing conditions, the molecular weight, the number of functional groups, the crosslinking density, the bulkiness of substituents, and the like. In the second embodiment, a resin having a property of being hard in a high-temperature environment is selected from commercially available resins as a resin for forming the surface coating layer 6, a resin composition for forming the surface coating layer 6 is prepared, the logarithmic decrement ΔE at 110° C. is measured, and a resin having a logarithmic decrement ΔE of 0.200 or less can be adopted for the surface coating layer 6.

For the surface coating layer 6 in the present disclosure, examples of the resin that forms the base material layer 1 include resins such as polyvinylidene chloride, polyester, polyamide, epoxy resin, acrylic resin, fluororesin, polyurethane, silicone resin and phenol resin, and modified products of these resins. The resin may be a copolymer of these resins or a modified product of the copolymer. Further, a mixture of these resins may be used. The resin is preferably a curable resin. That is, it is preferable that the surface coating layer 6 includes a cured product of a resin composition containing a curable resin.

The resin may be any of a one-liquid curable type and a two-liquid curable type, preferably a two-liquid curable type. Examples of the two-liquid curable resin include two-liquid curable polyurethane, two-liquid curable polyester and two-liquid curable epoxy resins. Of these, two-liquid curable polyurethane is preferable.

Examples of the two-liquid curable polyurethane include polyurethane which contains a first component containing a polyol compound and a second component containing an isocyanate compound. The polyurethane is preferably a two-liquid curable polyurethane adhesive having polyol such as polyester polyol, polyether polyol or acrylic polyol as a first component, and aromatic or aliphatic polyisocyanate as a second component. Examples of the polyurethane include polyurethane containing an isocyanate compound and a polyurethane compound obtained by reacting a polyol compound with an isocyanate compound in advance. Examples of the polyurethane include polyurethane containing a polyurethane compound and a polyurethane compound obtained by reacting a polyol compound with an isocyanate compound in advance. Examples of the polyurethane include polyurethane obtained by reacting a polyol compound with an isocyanate compound to form a polyurethane compound in advance, and reacting the polyurethane compound with moisture in the air or the like. It is preferable that polyester polyol having a hydroxyl group in the side chain in addition to a hydroxyl group at the end of the repeating unit is used as the polyol compound. Examples of the second component include aliphatic, alicyclic, aromatic and araliphatic isocyanate-based compounds. Examples of the isocyanate-based compound include hexamethylene diisocyanate (HDI), xylylene diisocyanate (XDI), isophorone diisocyanate (IPDI), hydrogenated XDI (H6XDI), hydrogenated MDI (H 12 MDI), tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI) and naphthalene diisocyanate (NDI). Examples of the isocyanate-based compound also include polyfunctional isocyanate-modified products of one or more of these diisocyanates can be mentioned. It is also possible to use a multimer (e.g. a trimer) as the polyisocyanate compound. Examples of the multimer include adducts, biurets, and nurates. The aliphatic isocyanate-based compound is an isocyanate having an aliphatic group and having no aromatic ring, the alicyclic isocyanate-based compound is an isocyanate having an alicyclic hydrocarbon group, and the aromatic isocyanate-based compound is an isocyanate having an aromatic ring. Since the surface coating layer 6 is formed of polyurethane, excellent electrolytic solution resistance is imparted to the exterior material for electrical storage devices.

In the first embodiment, it is preferable that the pressure sensitive adhesive component of the pressure sensitive adhesive tape and the resin contained in the resin composition for forming the surface coating layer 6 contains a common component form the viewpoint of more suitably enhancing adhesion between the pressure sensitive adhesive tape and the surface coating layer 6. In the pressure sensitive adhesive tape, for example, a pressure sensitive adhesive such as a synthetic rubber-based pressure sensitive adhesive, an acryl-based pressure sensitive adhesive or a silicone-based pressure sensitive adhesive is used as a pressure sensitive adhesive component, and among them, an acryl-based pressure sensitive adhesive is commonly used. Therefore, the resin contained in the resin composition for forming the surface coating layer 6 in the first embodiment is preferably an acrylic resin. Two-liquid polyurethane having an acrylic polyol as a first component is preferable.

When the resin in the resin composition forming the surface coating layer 6 in the first embodiment is polyurethane containing a first component containing a polyol compound and a second component containing an isocyanate compound, the logarithmic decrement ΔE at 60° C. or 30° C. can also be adjusted by, for example, adjusting the ratio between the first component and the second component.

If necessary, the surface coating layer 6 in the first embodiment may contain additives such as a filler, a slipping agent, an anti-blocking agent, a matting agent, a flame retardant, an antioxidant, a tackifier and an anti-static agent on at least one of the surface and the inside of the surface coating layer 6 according to the functionality and the like to be imparted to the surface coating layer 6 and the surface thereof. The additives are in the form of, for example, fine particles having an average particle diameter of about 0.5 nm to 5 μm. The average particle diameter of the additives is a median diameter measured by a laser diffraction/scattering particle size distribution measuring apparatus.

In the first embodiment, the additives may be either inorganic substances or organic substances. The shape of the additive is not particularly limited, and examples thereof include a spherical shape, a fibrous shape, a plate shape, an amorphous shape and a scaly shape.

In the first embodiment, specific examples of the additives include talc, silica, graphite, kaolin, montmorillonite, mica, hydrotalcite, silica gel, zeolite, aluminum hydroxide, magnesium hydroxide, zinc oxide, magnesium oxide, aluminum oxide, neodymium oxide, antimony oxide, titanium oxide, cerium oxide, calcium sulfate, barium sulfate, calcium carbonate, calcium silicate, lithium carbonate, calcium benzoate, calcium oxalate, magnesium stearate, alumina, carbon black, carbon nanotubes, high-melting-point nylons, acrylate resins, crosslinked acryl, crosslinked styrene, crosslinked polyethylene, benzoguanamine, gold, aluminum, copper and nickel. The additives may be used alone, or may be used in combination of two or more thereof. Of these additives, silica, barium sulfate and titanium oxide are preferable from the viewpoint of dispersion stability, costs, and so on. The surface of the additive may be subjected to various kinds of surface treatments such as insulation treatment and dispersibility enhancing treatment.

In the first embodiment, the filler, among additives, is preferably particles. Examples of the filler include inorganic fillers (preferably inorganic particles) and organic fillers (preferably organic particles). The surface coating layer 6 may contain one filler or two or more fillers. It is also preferable to use an inorganic filler and an organic filler in combination. The shape of the filler is not particularly limited, and examples thereof include a spherical shape, a fibrous shape, a plate shape, an amorphous shape and a scaly shape.

When the resin in the resin composition forming the surface coating layer 6 in the second embodiment is polyurethane containing a first component (main agent) containing a polyol compound and a second component (curing agent) containing an isocyanate compound, the logarithmic decrement ΔE at 110° C. can also be adjusted by, for example, adjusting the ratio between the first component and the second component.

It is preferable that the surface coating layer 6 in the present disclosure contains a resin and a filler. In the second embodiment, a matte-toned design can be imparted to the surface coating layer 6 when a filler is contained. The filler is preferably particles. Examples of the filler include inorganic fillers (preferably inorganic particles) and organic fillers (preferably organic particles). When the surface coating layer 6 in the second embodiment contains a filler, the surface coating layer 6 may contain one filler or two or more fillers. It is also preferable to use an inorganic filler and an organic filler in combination. The shape of the filler is not particularly limited, and examples thereof include a spherical shape, a fibrous shape, a plate shape, an amorphous shape and a scaly shape.

In the present disclosure, the average particle diameter of the filler is not particularly limited, and is, for example, about 0.01 to 5 μm from the viewpoint of ensuring that the exterior material 10 for electrical storage devices has a matte-toned design. The average particle size of the filler is a median diameter measured by a laser diffraction/scattering particle size distribution measuring apparatus. The average particle diameter of the filler is preferably equal to or less than the thickness of the surface coating layer 6.

In the present disclosure, the inorganic filler is preferably one capable of making the surface coating layer 6 matte-toned, and is not particularly limited, and examples thereof include particles of silica, talc, graphite, kaolin, montmorillonite, mica, hydrotalcite, silica gel, zeolite, aluminum hydroxide, magnesium hydroxide, zinc oxide, magnesium oxide, aluminum oxide, neodymium oxide, antimony oxide, titanium oxide, cerium oxide, calcium sulfate, barium sulfate, calcium carbonate, calcium silicate, lithium carbonate, calcium benzoate, calcium oxalate, magnesium stearate, alumina, carbon black, carbon nanotubes, gold, aluminum, copper and nickel. Of these, silica particles are particularly preferable.

In the present disclosure, the organic filler is not particularly limited as long as the surface coating layer 6 can have a matte tone, and examples thereof include particles of nylon, polyacrylate, polystyrene, polyethylene, benzoguanamine and crosslinked products thereof.

The content of the filler contained in the surface coating layer 6 in the first embodiment is not particularly limited as long as the logarithmic decrement ΔE of the outer surface of the surface coating layer 6 is 0.120 or less at 60° C. in measurement with a rigid body pendulum, and the content is preferably about 3 parts by mass or more, more preferably about 10 parts by mass or more, and preferably about 30 parts by mass or less, more preferably about 20 parts by mass or less, and is preferably in the range of about 3 to 30 parts by mass, about 3 to 20 parts by mass, about 10 to 30 parts by mass, or about 10 to 20 parts by mass, based on 100 parts by mass of the resin in the resin composition forming the surface coating layer 6.

The content of the filler contained in the surface coating layer 6 in the second embodiment is not particularly limited as long as the logarithmic decrement ΔE of the outer surface of the surface coating layer 6 is 0.200 or less at 110° C. in measurement with a rigid body pendulum, and the content is preferably about 3 parts by mass or more, more preferably about 10 parts by mass or more, and preferably about 30 parts by mass or less, more preferably about 20 parts by mass or less, and is preferably in the range of about 3 to 30 parts by mass, about 3 to 20 parts by mass, about 10 to 30 parts by mass, or about 10 to 20 parts by mass, based on 100 parts by mass of the resin in the resin composition forming the surface coating layer 6.

If necessary, the surface coating layer 6 may further contain additives such as a slipping agent and a colorant as described later, an anti-blocking agent, a flame retardant, an antioxidant, a tackifier and an anti-static agent on at least one of the surface and the inside of the surface coating layer 6 in the present disclosure according to the functionality and the like to be imparted to the surface coating layer 6 and the surface thereof.

In the present disclosure, when the surface coating layer 6 contains a colorant, a known colorant such as pigments and dyes can be used as the colorant. The colorants may be used alone, or may be used in combination of two or more thereof. Specific examples of the colorant contained in the surface coating layer 6 include the same colorants as those exemplified in the section [Adhesive agent Layer 2]. The preferred content of the colorant contained in the surface coating layer 6 is also the same as the content described in the section [Adhesive Agent Layer 2].

In the present disclosure, the slipping agent is not particularly limited, and is preferably an amide-based slipping agent. Specific examples of the amide-based slipping agent include saturated fatty acid amides, unsaturated fatty acid amides, substituted amides, methylol amides, saturated fatty acid bisamides, unsaturated fatty acid bisamides, fatty acid ester amides, and aromatic bisamides. Specific examples of the saturated fatty acid amide include lauric acid amide, palmitic acid amide, stearic acid amide, behenic acid amide, and hydroxystearic acid amide. Specific examples of unsaturated fatty acid amide include oleic acid amide and erucic acid amide. Specific examples of the substituted amide include N-oleylpalmitic acid amide, N-stearyl stearic acid amide, N-stearyl oleic acid amide, N-oleyl stearic acid amide, and N-stearyl erucic acid amide. Specific examples of the methylolamide include methylolstearic acid amide. Specific examples of the saturated fatty acid bisamide include methylenebisstearic acid amide, ethylenebiscapric acid amide, ethylenebislauric acid amide, ethylenebisstearic acid amide, ethylenebishydroxystearic acid amide, ethylenebisbehenic acid amide, hexamethylenebisstearic acid amide, hexamethylenehydroxystearic acid amide, N,N′-distearyl adipic acid amide, and N,N′-distearyl sebacic acid amide. Specific examples of the unsaturated fatty acid bisamide include ethylenebisoleic acid amide, ethylenebiserucic acid amide, hexamethylenebisoleic acid amide, N,N′-dioleyladipic acid amide, and N,N′-dioleylsebacic acid amide. Specific examples of the fatty acid ester amide include stearoamideethyl stearate. Specific examples of the aromatic bisamide include m-xylylenebisstearic acid amide, m-xylylenebishydroxystearic acid amide, and N,N′-distearylisophthalic acid amide. The slipping agents may be used alone, or may be used in combination of two or more thereof.

In the present disclosure, when the slipping agent is present on the surface of the surface coating layer 6, the amount of the slipping agent present is not particularly limited, and is preferably about 3 mg/m² or more, more preferably about 4 to 15 mg/m², still more preferably about 5 to 14 mg/m².

In the present disclosure, the slipping agent present on the surface of the surface coating layer 6 may be one obtained by exuding the slipping agent contained in the resin forming the surface coating layer 6, or one obtained by applying the slipping agent to the surface of the surface coating layer 6.

In the present disclosure, the method for forming the surface coating layer 6 is not particularly limited, and examples thereof include a method in which a resin for forming the surface coating layer 6 is applied. When the additive is added to the surface coating layer 6, a resin mixed with the additive may be applied.

In the present disclosure, the thickness of the surface coating layer 6 is not particularly limited as long as the above-mentioned function as the surface coating layer 6 is performed, and it is, for example, about 0.5 to 10 μm, preferably about 1 to 5 μm.

[Base Material Layer 1]

In the present disclosure, the base material layer 1 is a layer provided for the purpose of, for example, exhibiting a function as a base material of the exterior material for electrical storage devices. The base material layer 1 is located between the surface coating layer 6 and the barrier layer 3 of the exterior material 10 for electrical storage devices. When the adhesive agent layer 2 is present, the adhesive agent layer 2 is located between the surface coating layer 6 and the adhesive agent layer 2.

The material that forms the base material layer 1 is not particularly limited as long as it has a function as a base material, i.e. at least insulation quality. The base material layer 1 can be formed using, for example, a resin, and the resin may contain additives described later.

When the base material layer 1 is formed of a resin, the base material layer 1 may be, for example, a resin film formed of a resin, or may be formed by applying a resin. The resin film may be an unstretched film or a stretched film. Examples of the stretched film include uniaxially stretched films and biaxially stretched films, and biaxially stretched films are preferable. Examples of the stretching method for forming a biaxially stretched film include a sequential biaxial stretching method, an inflation method, and a simultaneous biaxial stretching method. Examples of the method for applying a resin include a roll coating method, a gravure coating method and an extrusion coating method.

Examples of the resin that forms the base material layer 1 include resins such as polyester, polyamide, polyolefin, epoxy resin, acrylic resin, fluororesin, polyurethane, silicone resin and phenol resin, and modified products of these resins. The resin that forms the base material layer 1 may be a copolymer of these resins or a modified product of the copolymer. Further, a mixture of these resins may be used.

Of these resins, polyester and polyamide are preferable as resins that form the base material layer 1.

Specific examples of the polyester include polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polybutylene naphthalate, polyethylene isophthalate, and copolyesters. Examples of the copolyester include copolyesters having ethylene terephthalate as a main repeating unit. Specific examples thereof include copolymer polyesters that are polymerized with ethylene isophthalate and include ethylene terephthalate as a main repeating unit (hereinafter, abbreviated as follows after polyethylene(terephthalate/isophthalate)), polyethylene(terephthalate/adipate), polyethylene(terephthalate/sodium sulfoisophthalate), polyethylene(terephthalate/sodium isophthalate), polyethylene (terephthalate/phenyl-dicarboxylate) and polyethylene(terephthalate/decane dicarboxylate). These polyesters may be used alone, or may be used in combination of two or more thereof.

Specific examples of the polyamide include polyamides such as aliphatic polyamides such as nylon 6, nylon 66, nylon 610, nylon 12, nylon 46, and copolymers of nylon 6 and nylon 66; hexamethylenediamine-isophthalic acid-terephthalic acid copolymerization polyamides containing a structural unit derived from terephthalic acid and/or isophthalic acid, such as nylon 61, nylon 6T, nylon 61T and nylon 616T (I denotes isophthalic acid and T denotes terephthalic acid), and polyamides containing aromatics, such as polyamide MXD6 (polymethaxylylene adipamide); alicyclic polyamides such as polyamide PACM6 (polybis(4-aminocyclohexyl)methaneadipamide; polyamides copolymerized with a lactam component or an isocyanate component such as 4,4′-diphenylmethane-diisocyanate, and polyester amide copolymers and polyether ester amide copolymers as copolymers of a copolymerization polyamide and a polyester or a polyalkylene ether glycol; and copolymers thereof. These polyamides may be used alone, or may be used in combination of two or more thereof.

The base material layer 1 contains preferably at least one of a polyester film, a polyamide film and a polyolefin film, preferably at least one of a stretched polyester film, a stretched polyamide film and a stretched polyolefin film, still more preferably at least one of a stretched polyethylene terephthalate film, a stretched polybutylene terephthalate film, a stretched nylon film and a stretched polypropylene film, even more preferably at least one of a biaxially stretched polyethylene terephthalate film, a biaxially stretched polybutylene terephthalate film, a biaxially stretched nylon film, and a biaxially stretched polypropylene film.

The base material layer 1 may be a single layer, or may include two or more layers. When the base material layer 1 includes two or more layers, the base material layer 1 may be a laminate obtained by laminating resin films with an adhesive or the like, or a resin film laminate obtained by co-extruding resins to form two or more layers. The resin film laminate obtained by co-extruding resins to form two or more layers may be used as the base material layer 1 in an unstretched state, or may be uniaxially stretched or biaxially stretched and used as the base material layer 1.

Specific examples of the resin film laminate with two or more layers in the base material layer 1 include laminates of a polyester film and a nylon film, nylon film laminates with two or more layers, and polyester film laminates with two or more layers. Laminates of a stretched nylon film and a stretched polyester film, stretched nylon film laminates with two or more layers, and stretched polyester film laminates with two or more layers are preferable. For example, when the base material layer 1 is a resin film laminate with two layers, the base material layer 1 is preferably a laminate of a polyester resin film and a polyester resin film, a laminate of a polyamide resin film and a polyamide resin film, or a laminate of a polyester resin film and a polyamide resin film, more preferably a laminate of a polyethylene terephthalate film and a polyethylene terephthalate film, a laminate of a nylon film and a nylon film, or a laminate of a polyethylene terephthalate film and a nylon film. Since the polyester resin is hardly discolored even in the case where for example, an electrolytic solution is deposited on the surface, it is preferable that the polyester resin film is located on the outermost side of the base material layer 1 when the base material layer 1 is a resin film laminate with two or more layers.

When the base material layer 1 is a resin film laminate with two or more layers, the two or more resin films may be laminated with an adhesive interposed therebetween. Specific examples of the preferred adhesive include the same adhesives as those exemplified for the adhesive agent layer 2 described later. The method for laminating a resin film having two or more layers is not particularly limited, and a known method can be employed. Examples thereof include a dry lamination method, a sand lamination method, an extrusion lamination method and a thermal lamination method, and a dry lamination method is preferable. When the resin film is laminated by a dry lamination method, it is preferable to use a polyurethane adhesive as the adhesive. Here, the thickness of the adhesive is, for example, about 2 to 5 μm. In addition, the lamination may be performed with an anchor coat layer formed on the resin film. Examples of the anchor coat layer include the same adhesives as those exemplified for the adhesive agent layer 2 described later. Here, the thickness of the anchor coat layer is, for example, about 0.01 to 1.0 μm.

Additives such as a slipping agent, a flame retardant, an antiblocking agent, an antioxidant, a light stabilizer, a tackifier and an antistatic agent may be present on at least one of the surface of the base material layer 1 and/or inside the base material layer 1. The additives may be used alone, or may be used in combination of two or more thereof.

The thickness of the base material layer 1 is not particularly limited as long as a function as a base material is performed, and the thickness of the base material layer 1 is, for example, about 3 to 50 μm, preferably about 10 to 35 μm. When the base material layer 1 is a resin film laminate with two or more layers, the thickness of the resin film forming each layer is preferably about 2 to 25 μm.

[Adhesive Agent Layer 2]

In the exterior material for electrical storage devices of the present disclosure, the adhesive agent layer 2 is a layer provided between the base material layer 1 and the barrier layer 3 if necessary for the purpose of enhancing bondability between these layers.

The adhesive agent layer 2 is formed from an adhesive capable of bonding the base material layer 1 and the barrier layer 3. The adhesive used for forming the adhesive agent layer 2 is not limited, and may be any of a chemical reaction type, a solvent volatilization type, a heat melting type, a heat pressing type, and the like. The adhesive agent may be a two-liquid curable adhesive (two-liquid adhesive), a one-liquid curable adhesive (one-liquid adhesive), or a resin that does not involve curing reaction. The adhesive agent layer 2 may be a single layer or a multi-layer.

Specific examples of the adhesive component contained in the adhesive include polyester such as polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polybutylene naphthalate, polyethylene isophthalate and copolyester; polyether; polyurethane; epoxy resins; phenol resins; polyamides such as nylon 6, nylon 66, nylon 12 and copolymerized polyamide; polyolefin-based resins such as polyolefins, cyclic polyolefins, acid-modified polyolefins and acid-modified cyclic polyolefins; cellulose; (meth)acrylic resins; polyimide; polycarbonate; amino resins such as urea resins and melamine resins; rubbers such as chloroprene rubber, nitrile rubber and styrene-butadiene rubber; and silicone resins. These adhesive components may be used alone, or may be used in combination of two or more thereof. Of these adhesive components, polyurethane-based adhesives are preferable. In addition, the adhesive strength of these resins used as adhesive components can be increased by using an appropriate curing agent in combination. As the curing agent, appropriate one is selected from polyisocyanate, a polyfunctional epoxy resin, an oxazoline group-containing polymer, a polyamine resin, an acid anhydride and the like according to the functional group of the adhesive component.

Examples of the polyurethane adhesive include polyurethane adhesives containing a first component containing a polyol compound and a second component containing an isocyanate compound. The polyurethane adhesive is preferably a two-liquid curable polyurethane adhesive having polyol such as polyester polyol, polyether polyol or acrylic polyol as a first component, and aromatic or aliphatic polyisocyanate as a second component. Examples of the polyurethane adhesive include polyurethane adhesives containing an isocyanate compound and a polyurethane compound obtained by reacting a polyol compound with an isocyanate compound in advance. Examples of the polyurethane adhesive include polyurethane adhesives containing a polyol compound and a polyurethane compound obtained by reacting a polyol compound with an isocyanate compound in advance. Examples of the polyurethane adhesive include polyurethane adhesives obtained by reacting a polyol compound with an isocyanate compound to form a polyurethane compound in advance, and reacting the polyurethane compound with moisture in the air or the like. It is preferable that polyester polyol having a hydroxyl group in the side chain in addition to a hydroxyl group at the end of the repeating unit is used as the polyol compound. Examples of the second component include aliphatic, alicyclic, aromatic and araliphatic isocyanate-based compounds.

Examples of the isocyanate-based compound include hexamethylene diisocyanate (HDI), xylylene diisocyanate (XDI), isophorone diisocyanate (IPDI), hydrogenated XDI (H6XDI), hydrogenated MDI (H 12 MDI), tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI) and naphthalene diisocyanate (NDI). Examples of the isocyanate-based compound also include polyfunctional isocyanate-modified products of one or more of these diisocyanates can be mentioned. It is also possible to use a multimer (e.g. a trimer) as the polyisocyanate compound. Examples of the multimer include adducts, biurets, and nurates. Since the adhesive agent layer 2 is formed of a polyurethane adhesive, excellent electrolytic solution resistance is imparted to the exterior material for electrical storage devices, so that peeling of the base material layer 1 is suppressed even if the electrolytic solution is deposited on the side surface.

Other components may be added to the adhesive agent layer 2 as long as bondability is not inhibited, and the adhesive agent layer 2 may contain a colorant, a thermoplastic elastomer, a tackifier, a filler, and the like. When the adhesive agent layer 2 contains a colorant, the exterior material for electrical storage devices can be colored. As the colorant, known colorants such as pigments and dyes can be used. The colorants may be used alone, or may be used in combination of two or more thereof.

The type of pigment is not particularly limited as long as the bondability of the adhesive agent layer 2 is not impaired. Examples of the organic pigment include azo-based pigments, phthalocyanine-based pigments, quinacridone-based pigments, anthraquinone-based pigments, dioxazine-based pigments, indigothioindigo-based pigments, perinone-perylene-based pigments, isoindolenine-based pigments and benzimidazolone-based pigments. Examples of the inorganic pigment include carbon black-based pigments, titanium oxide-based pigments, cadmium-based pigments, lead-based pigments, chromium-based pigments, iron-based pigments and copper-based pigments and also fine powder of mica (mica) and fish scale foil.

Of the colorants, carbon black is preferable for the purpose of, for example, blackening the appearance of the exterior material for electrical storage devices.

The average particle diameter of the pigment is not particularly limited, and is, for example, about 0.05 to 5 μm, preferably about 0.08 to 2 μm. The average particle size of the pigment is a median diameter measured by a laser diffraction/scattering particle size distribution measuring apparatus.

The content of the pigment in the adhesive agent layer 2 is not particularly limited as long as the exterior material for electrical storage devices is colored, and the content is, for example, about 5 to 60 mass %, preferably 10 to 40 mass %.

The thickness of the adhesive agent layer 2 is not particularly limited as long as the base material layer 1 and the barrier layer 3 can be bonded to each other, and the thickness is, for example, about 1 μm or more, or about 2 μm or more. The thickness of the adhesive agent layer 2 is, for example, about 10 μm or less, or about 5 μm or less. The thickness of the adhesive agent layer 2 is preferably in the range of about 1 to 10 μm, about 1 to 5 μm, about 2 to 10 μm, or about 2 to 5 μm.

[Colored Layer]

The colored layer is a layer provided between the base material layer 1 and the barrier layer 3 if necessary (not shown). When the adhesive agent layer 2 is present, the colored layer may be provided between the base material layer 1 and the adhesive agent layer 2 or between the adhesive agent layer 2 and the barrier layer 3. The colored layer may be provided outside the base material layer 1. By providing the colored layer, the exterior material for electrical storage devices can be colored. The colored adhesive agent layer 2 and the colored layer and may be provided between the base material layer 1 and the barrier layer 3.

The colored layer can be formed by, for example, applying an ink containing a colorant to the surface of the base material layer 1, or the surface of the barrier layer 3. As the colorant, known colorants such as pigments and dyes can be used. The colorants may be used alone, or may be used in combination of two or more thereof.

Specific examples of the colorant contained in the colored layer include the same colorants as those exemplified in the section [Adhesive Agent Layer 2].

[Barrier Layer 3]

In the exterior material for electrical storage devices, the barrier layer 3 is a layer which suppresses at least ingress of moisture.

Examples of the barrier layer 3 include metal foils, deposited films and resin layers having a barrier property. Examples of the deposited film include metal deposited films, inorganic oxide deposited films and carbon-containing inorganic oxide deposited films, and examples of the resin layer include those of polyvinylidene chloride, fluorine-containing resins such as polymers containing chlorotrifluoroethylene (CTFE) as a main component, polymers containing tetrafluoroethylene (TFE) as a main component, polymers having a fluoroalkyl group, and polymers containing a fluoroalkyl unit as a main component, and ethylene vinyl alcohol copolymers. Examples of the barrier layer 3 include resin films provided with at least one of these deposited films and resin layers. A plurality of barrier layers 3 may be provided. Preferably, the barrier layer 3 contains a layer formed of a metal material. Specific examples of the metal material forming the barrier layer 3 include aluminum alloys, stainless steel, titanium steel and steel. When the metal material is used as a metal foil, it is preferable that the metal material includes at least one of an aluminum alloy foil and a stainless steel foil. Further, in the second embodiment, it is preferable that the metal material includes a stainless steel foil from the viewpoint of more suitably enhancing the damage resistance in a high-temperature environment.

The aluminum alloy is more preferably a soft aluminum alloy foil formed of, for example, an annealed aluminum alloy from the viewpoint of improving the moldability of the exterior material for electrical storage devices, and is preferably an aluminum alloy foil containing iron from the viewpoint of further improving the moldability. In the aluminum alloy foil containing iron (100 mass %), the content of iron is preferably 0.1 to 9.0 mass %, more preferably 0.5 to 2.0 mass %. When the content of iron is 0.1 mass % or more, it is possible to obtain an exterior material for electrical storage devices which has more excellent moldability. When the content of iron is 9.0 mass % or less, it is possible to obtain an exterior material for electrical storage devices which is more excellent in flexibility. Examples of the soft aluminum alloy foil include aluminum alloy foils having a composition specified in JIS H4160: 1994 A8021H-O, JIS H4160: 1994 A8079H-O, JIS H4000: 2014 A8021P-O, or JIS H4000: 2014 A8079P-O. If necessary, silicon, magnesium, copper, manganese or the like may be added. Softening can be performed by annealing or the like.

Examples of the stainless steel foil include austenitic stainless steel foils, ferritic stainless steel foils, austenitic/ferritic stainless steel foils, martensitic stainless steel foils and precipitation-hardened stainless steel foils. From the viewpoint of providing an exterior material for electrical storage devices which is further excellent in moldability, it is preferable that the stainless steel foil is formed of austenitic stainless steel.

Specific examples of the austenite-based stainless steel foil include SUS 304 stainless steel, SUS 301 stainless steel and SUS 316L stainless steel, and of these, SUS 304 stainless steel is especially preferable.

When the barrier layer 3 is a metal foil, the barrier layer 3 may perform a function as a barrier layer suppressing at least ingress of moisture, and has a thickness of, for example, about 9 to 200 μm. The thickness of the barrier layer 3 is preferably about 85 μm or less, more preferably about 50 μm or less, still more preferably about 40 μm or less, particularly preferably about 35 μm or less. The thickness of the barrier layer 3 is preferably about 10 μm or more, more preferably about 20 μm or more, still more preferably about 25 μm or more. The total thickness of the barrier layer 3 is preferably in the range of about 10 to 85 μm, about 10 to 50 μm, about 10 to 40 μm, about 10 to 35 μm, about 20 to 85 μm, about 20 to 50 μm, about 20 to 40 μm, about 20 to 35 μm, about 25 to 85 μm, about 25 to 50 μm, about 25 to 40 μm, or about 25 to 35 μm. When the barrier layer 3 is formed of an aluminum alloy foil, the thickness thereof is especially preferably in above-described range. In particular, when the barrier layer 3 includes a stainless steel foil, the thickness of the stainless steel foil is preferably about 60 μm or less, more preferably about 50 μm or less, still more preferably about 40 μm or less, even more preferably about 30 μm or less, particularly preferably about 25 μm or less. The thickness of the stainless steel foil is preferably about 10 μm or more, more preferably about 15 μm or more. The thickness of the stainless steel foil is preferably in the range of about 10 to 60 μm, about 10 to 50 μm, about 10 to 40 μm, about 10 to 30 μm, about 10 to 25 μm, about 15 to 60 μm, about 15 to 50 μm, about 15 to 40 μm, about 15 to 30 μm, or about 15 to 25 μm.

When the barrier layer 3 is a metal foil, it is preferable that a corrosion-resistant film is provided at least on a surface on a side opposite to the base material layer for preventing dissolution and corrosion. The barrier layer 3 may include a corrosion-resistant film on each of both surfaces. Here, the corrosion-resistant film refers to a thin film obtained by subjecting the surface of the barrier layer to, for example, hydrothermal denaturation treatment such as boehmite treatment, chemical conversion treatment, anodization treatment, plating treatment with nickel, chromium or the like, or corrosion prevention treatment by applying a coating agent to impart corrosion resistance (e.g. acid resistance and alkali resistance) to the barrier layer. Specifically, the corrosion-resistant film means a film which improves the acid resistance of the barrier layer (acid-resistant film), a film which improves the alkali resistance of the barrier layer (alkali-resistant film), or the like. One of treatments for forming the corrosion-resistant film may be performed, or two or more thereof may be performed in combination. In addition, not only one layer but also multiple layers can be formed. Further, of these treatments, the hydrothermal denaturation treatment and the anodization treatment are treatments in which the surface of the metal foil is dissolved with a treatment agent to form a metal compound excellent in corrosion resistance. The definition of the chemical conversion treatment may include these treatments. When the barrier layer 3 is provided with the corrosion-resistant film, the barrier layer 3 is regarded as including the corrosion-resistant film.

The corrosion-resistant film exhibits the effects of preventing delamination between the barrier layer (e.g. an aluminum alloy foil) and the base material layer during molding of the exterior material for electrical storage devices; preventing dissolution and corrosion of the surface of the barrier layer, particularly dissolution and corrosion of aluminum oxide present on the surface of the barrier layer when the barrier layer is an aluminum alloy foil, by hydrogen fluoride generated by reaction of an electrolyte with moisture; improving the bondability (wettability) of the surface of the barrier layer; preventing delamination between the base material layer and the barrier layer during heat-sealing; and preventing delamination between the base material layer and the barrier layer during molding.

Various corrosion-resistant films formed by chemical conversion treatment are known, and examples thereof include mainly corrosion-resistant films containing at least one of a phosphate, a chromate, a fluoride, a triazine thiol compound, and a rare earth oxide. Examples of the chemical conversion treatment using a phosphate or a chromate include chromic acid chromate treatment, phosphoric acid chromate treatment, phosphoric acid-chromate treatment and chromate treatment, and examples of the chromium compound used in these treatments include chromium nitrate, chromium fluoride, chromium sulfate, chromium acetate, chromium oxalate, chromium biphosphate, acetylacetate chromate, chromium chloride and chromium potassium sulfate. Examples of the phosphorus compound used in these treatments include sodium phosphate, potassium phosphate, ammonium phosphate and polyphosphoric acid. Examples of the chromate treatment include etching chromate treatment, electrolytic chromate treatment and coating-type chromate treatment, and coating-type chromate treatment is preferable. This coating-type chromate treatment is treatment in which at least a surface of the barrier layer (e.g. an aluminum alloy foil) on the inner layer side is first degreased by a well-known treatment method such as an alkali immersion method, an electrolytic cleaning method, an acid cleaning method, an electrolytic acid cleaning method or an acid activation method, and a treatment solution containing a metal phosphate such as Cr (chromium) phosphate, Ti (titanium) phosphate, Zr (zirconium) phosphate or Zn (zinc) phosphate or a mixture of these metal salts as a main component, a treatment solution containing any of non-metal salts of phosphoric acid and a mixture of these non-metal salts as a main component, or a treatment solution formed of a mixture of any of these salts and a synthetic resin or the like is then applied to the degreased surface by a well-known coating method such as a roll coating method, a gravure printing method or an immersion method, and dried. As the treatment liquid, for example, various solvents such as water, an alcohol-based solvent, a hydrocarbon-based solvent, a ketone-based solvent, an ester-based solvent, and an ether-based solvent can be used, and water is preferable. Examples of the resin component used here include polymers such as phenol-based resins and acryl-based resins, and examples of the treatment include chromate treatment using an aminated phenol polymer having any of repeating units represented by the following general formulae (1) to (4). In the aminated phenol polymer, the repeating units represented by the following general formulae (1) to (4) may be contained alone, or may be contained in combination of two or more thereof. The acryl-based resin is preferably polyacrylic acid, an acrylic acid-methacrylic acid ester copolymer, an acrylic acid-maleic acid copolymer, an acrylic acid-styrene copolymer, or a derivative thereof such as a sodium salt, an ammonium salt or an amine salt thereof. In particular, a derivative of polyacrylic acid such as an ammonium salt, a sodium salt or an amine salt of polyacrylic acid is preferable. In the present disclosure, the polyacrylic acid means a polymer of acrylic acid. The acryl-based resin is also preferably a copolymer of acrylic acid and dicarboxylic acid or dicarboxylic anhydride, and is also preferably an ammonium salt, a sodium salt or an amine salt of a copolymer of acrylic acid and dicarboxylic acid or dicarboxylic anhydride. The acryl-based resins may be used alone, or may be used in combination of two or more thereof.

In the general formulae (1) to (4), X represents a hydrogen atom, a hydroxy group, an alkyl group, a hydroxyalkyl group, an allyl group, or a benzyl group. R¹ and R² are the same or different, and each represents a hydroxy group, an alkyl group, or a hydroxyalkyl group. In the general formulae (1) to (4), examples of the alkyl group represented by X, R¹ and R² include linear or branched alkyl groups with a carbon number of 1 to 4, such as a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, and a tert-butyl group. Examples of the hydroxyalkyl group represented by X, R¹ and R² include linear or branched alkyl groups with a carbon number of 1 to 4, which is substituted with one hydroxy group, such as a hydroxymethyl group, a 1-hydroxyethyl group, a 2-hydroxyethyl group, a 1-hydroxypropyl group, a 2-hydroxypropyl group, a 3-hydroxypropyl group, a 1-hydroxybutyl group, a 2-hydroxybutyl group, a 3-hydroxybutyl group, and a 4-hydroxybutyl group. In the general formulae (1) to (4), the alkyl group and the hydroxyalkyl group represented by X, R¹ and R² may be the same or different. In the general formulae (1) to (4), X is preferably a hydrogen atom, a hydroxy group or a hydroxyalkyl group. A number average molecular weight of the aminated phenol polymer having repeating units represented by the general formulae (1) to (4) is preferably about 500 to 1,000,000, and more preferably about 1,000 to 20,000, for example. The aminated phenol polymer is produced by, for example, performing polycondensation of a phenol compound or a naphthol compound with formaldehyde to prepare a polymer including repeating units represented by the general formula (1) or the general formula (3), and then introducing a functional group (—CH₂NR¹R²) into the obtained polymer using formaldehyde and an amine (R¹R²NH). The aminated phenol polymers are used alone, or used in combination of two or more thereof.

Other examples of the corrosion-resistant film include thin films formed by corrosion prevention treatment of coating type in which a coating agent containing at least one selected from the group consisting of a rare earth element oxide sol, an anionic polymer and a cationic polymer is applied. The coating agent may further contain phosphoric acid or a phosphate, and a crosslinker for crosslinking the polymer. In the rare earth element oxide sol, fine particles of a rare earth element oxide (e.g. particles having an average particle diameter of 100 nm or less) are dispersed in a liquid dispersion medium. Examples of the rare earth element oxide include cerium oxide, yttrium oxide, neodymium oxide and lanthanum oxide, and cerium oxide is preferable from the viewpoint of further improving adhesion. The rare earth element oxides contained in the corrosion-resistant film can be used alone, or used in combination of two or more thereof. As the liquid dispersion medium for the rare earth element oxide, for example, various solvents such as water, an alcohol-based solvent, a hydrocarbon-based solvent, a ketone-based solvent, an ester-based solvent, and an ether-based solvent can be used, and water is preferable. For example, the cationic polymer is preferably polyethyleneimine, an ion polymer complex formed of a polymer having polyethyleneimine and a carboxylic acid, primary amine-grafted acrylic resins obtained by graft-polymerizing a primary amine with an acrylic main backbone, polyallylamine or a derivative thereof, or aminated phenol. The anionic polymer is preferably poly (meth)acrylic acid or a salt thereof, or a copolymer containing (meth)acrylic acid or a salt thereof as a main component. The crosslinker is preferably at least one selected from the group consisting of a silane coupling agent and a compound having any of functional groups including an isocyanate group, a glycidyl group, a carboxyl group and an oxazoline group. In addition, the phosphoric acid or phosphate is preferably condensed phosphoric acid or a condensed phosphate.

Examples of the corrosion-resistant film include films formed by applying a dispersion of fine particles of a metal oxide such as aluminum oxide, titanium oxide, cerium oxide or tin oxide or barium sulfate in phosphoric acid to the surface of the barrier layer and performing baking treatment at 150° C. or higher.

The corrosion-resistant film may have a laminated structure in which at least one of a cationic polymer and an anionic polymer is further laminated if necessary. Examples of the cationic polymer and the anionic polymer include those described above.

The composition of the corrosion-resistant film can be analyzed by, for example, time-of-flight secondary ion mass spectrometry.

The amount of the corrosion-resistant film to be formed on the surface of the barrier layer 3 in the chemical conversion treatment is not particularly limited, but for example when the coating-type chromate treatment is performed, and it is desirable that the chromic acid compound be contained in an amount of, for example, about 0.5 to 50 mg, preferably about 1.0 to 40 mg, in terms of chromium, the phosphorus compound be contained in an amount of, for example, about 0.5 to 50 mg, preferably about 1.0 to 40 mg, in terms of phosphorus, and the aminated phenol polymer be contained in an amount of, for example, about 1.0 to 200 mg, preferably about 5.0 to 150 mg, per 1 m² of the surface of the barrier layer 3.

The thickness of the corrosion-resistant film is not particularly limited, and is preferably about 1 nm to 20 μm, more preferably about 1 nm to 100 nm, still more preferably about 1 nm to 50 nm from the viewpoint of the cohesive force of the film and the adhesive strength with the barrier layer and the heat-sealable resin layer. The thickness of the corrosion-resistant film can be measured by observation with a transmission electron microscope or a combination of observation with a transmission electron microscope and energy dispersive X-ray spectroscopy or electron beam energy loss spectroscopy. By analyzing the composition of the corrosion-resistant film using time-of-flight secondary ion mass spectrometry, peaks derived from secondary ions from, for example, Ce, P and O (e.g. at least one of Ce₂PO₄ ⁺, CePO₄ ⁻ and the like) and secondary ions from, for example, Cr, P and O (e.g. at least one of CrPO₂ ⁺, CrPO₄ ⁻ and the like) are detected.

The chemical conversion treatment is performed in the following manner: a solution containing a compound to be used for formation of a corrosion-resistant film is applied to the surface of the barrier layer by a bar coating method, a roll coating method, a gravure coating method, an immersion method or the like, and heating is then performed so that the temperature of the barrier layer is about 70 to about 200° C. The barrier layer may be subjected to a degreasing treatment by an alkali immersion method, an electrolytic cleaning method, an acid cleaning method, an electrolytic acid cleaning method or the like before the barrier layer is subjected to a chemical conversion treatment. When a degreasing treatment is performed as described above, the chemical conversion treatment of the surface of the barrier layer can be further efficiently performed. When an acid degreasing agent with a fluorine-containing compound dissolved in an inorganic acid is used for degreasing treatment, not only a metal foil degreasing effect can be obtained but also a metal fluoride can be formed as a passive state, and in this case, only degreasing treatment may be performed.

[Heat-Sealable Resin Layer 4]

In the exterior material for electrical storage devices according to the present disclosure, the heat-sealable resin layer 4 is a layer (sealant layer) which corresponds to an innermost layer and performs a function of hermetically sealing the electrical storage device element by heat-sealing the heat-sealable resin layer during construction of the electrical storage device.

The resin forming the heat-sealable resin layer 4 is not particularly limited as long as it can be heat-sealed, a resin containing a polyolefin backbone such as a polyolefin or an acid-modified polyolefin is preferable. The resin forming the heat-sealable resin layer 4 can be confirmed to contain a polyolefin backbone by an analysis method such as infrared spectroscopy or gas chromatography-mass spectrometry. It is preferable that a peak derived from maleic anhydride is detected when the resin forming the heat-sealable resin layer 4 is analyzed by infrared spectroscopy. For example, when a maleic anhydride-modified polyolefin is measured by infrared spectroscopy, peaks derived from maleic anhydride are detected near wavenumbers of 1760 cm⁻¹ and 1780 cm⁻¹. When the heat-sealable resin layer 4 is a layer formed of a maleic anhydride-modified polyolefin, a peak derived from maleic anhydride is detected when measurement is performed by infrared spectroscopy. However, if the degree of acid modification is low, the peaks may be too small to be detected. In that case, the peaks can be analyzed by nuclear magnetic resonance spectroscopy.

Specific examples of the polyolefin include polyethylenes such as low-density polyethylene, medium-density polyethylene, high-density polyethylene and linear low-density polyethylene; ethylene-α-olefin copolymers; polypropylene such as homopolypropylene, block copolymers of polypropylene (e.g., block copolymers of propylene and ethylene) and random copolymers of polypropylene (e.g., random copolymers of propylene and ethylene); propylene-α-olefin copolymers; and terpolymers of ethylene-butene-propylene. Of these, polypropylene is preferable. The polyolefin resin in the case of a copolymer may be a block copolymer or a random copolymer. These polyolefin-based resins may be used alone, or may be used in combination of two or more thereof.

The polyolefin may be a cyclic polyolefin. The cyclic polyolefin is a copolymer of an olefin and a cyclic monomer, and examples of the olefin as a constituent monomer of the cyclic polyolefin include ethylene, propylene, 4-methyl-1-pentene, styrene, butadiene and isoprene. Examples of the cyclic monomer as a constituent monomer of the cyclic polyolefin include cyclic alkenes such as norbornene; cyclic dienes such as cyclopentadiene, dicyclopentadiene, cyclohexadiene and norbornadiene. Among these polyolefins, cyclic alkenes are preferable, and norbornene is more preferable.

The acid-modified polyolefin is a polymer with the polyolefin modified by subjecting the polyolefin to block polymerization or graft polymerization with an acid component. As the polyolefin to be acid-modified, the above-mentioned polyolefins, copolymers obtained by copolymerizing polar molecules such as acrylic acid or methacrylic acid with the above-mentioned polyolefins, polymers such as crosslinked polyolefins, or the like can also be used. Examples of the acid component to be used for acid modification include carboxylic acids such as maleic acid, acrylic acid, itaconic acid, crotonic acid, maleic anhydride and itaconic anhydride, and anhydrides thereof.

The acid-modified polyolefin may be an acid-modified cyclic polyolefin. The acid-modified cyclic polyolefin is a polymer obtained by copolymerizing a part of monomers forming the cyclic polyolefin in place of an acid component, or block-polymerizing or graft-polymerizing an acid component with the cyclic polyolefin. The cyclic polyolefin to be modified with an acid is the same as described above. The acid component to be used for acid modification is the same as the acid component used for modification of the polyolefin.

Examples of preferred acid-modified polyolefins include polyolefins modified with a carboxylic acid or an anhydride thereof, polypropylene modified with a carboxylic acid or an anhydride thereof, maleic anhydride-modified polyolefins, and maleic anhydride-modified polypropylene.

The heat-sealable resin layer 4 may be formed from one resin alone, or may be formed from a blend polymer obtained by combining two or more resins. Further, the heat-sealable resin layer 4 may be composed of only one layer, or may be composed of two or more layers with the same resin component or different resin components.

The heat-sealable resin layer 4 may contain a slipping agent etc. if necessary. When the heat-sealable resin layer 4 contains a slipping agent, the moldability of the exterior material for electrical storage devices can be improved. The slipping agent is not particularly limited, and a known slipping agent can be used. The slipping agents may be used alone, or may be used in combination of two or more thereof.

The slipping agent is not particularly limited, and is preferably an amide-based slipping agent. Specific examples of the slipping agent include those exemplified for the base material layer 1. The slipping agents may be used alone, or may be used in combination of two or more thereof.

When a slipping agent is present on the surface of the heat-sealable resin layer 4, the amount of the slipping agent present is not particularly limited, and is preferably about 10 to 50 mg/m², more preferably about 15 to 40 mg/m² from the viewpoint of improving the moldability of the exterior material for electrical storage devices.

The slipping agent present on the surface of the heat-sealable resin layer 4 may be one obtained by exuding the slipping agent contained in the resin forming the heat-sealable resin layer 4, or one obtained by applying a slipping agent to the surface of the heat-sealable resin layer 4.

The thickness of the heat-sealable resin layer 4 is not particularly limited as long as the heat-sealable resin layers are heat-sealed to each other to perform a function of sealing the electrical storage device element, and the thickness is, for example, about 100 μm or less, preferably about 85 μm or less, more preferably about 15 to 85 μm. For example, when the thickness of the adhesive layer 5 described later is 10 μm or more, the thickness of the heat-sealable resin layer 4 is preferably about 85 μm or less, more preferably about 15 to 45 μm. For example, when the thickness of the adhesive layer 5 described later is less than 10 μm or the adhesive layer 5 is not provided, the thickness of the heat-sealable resin layer 4 is preferably about 20 μm or more, more preferably about 35 to 85 μm.

[Adhesive Layer 5]

In the exterior material for electrical storage devices according to the present disclosure, the adhesive layer 5 is a layer provided between the barrier layer 3 (or corrosion-resistant film) and the heat-sealable resin layer 4 if necessary for firmly bonding these layers to each other.

The adhesive layer 5 is formed from a resin capable of bonding the barrier layer 3 and the heat-sealable resin layer 4 to each other. The resin to be used for forming the adhesive layer 5 is, for example, the same as that of the adhesive exemplified for the adhesive agent layer 2. From the viewpoint of firmly bonding the adhesive layer 5 to the heat-sealable resin layer 4, it is preferable that the resin to be used for forming the adhesive layer 5 contains a polyolefin backbone. Examples thereof include the polyolefins and acid-modified polyolefins exemplified for the heat-sealable resin layer 4 described above. On the other hand, from the viewpoint of firmly bonding the barrier layer 3 and the adhesive layer 5 to each other, it is preferable that the adhesive layer 5 contains an acid-modified polyolefin. Examples of the acid modifying component include dicarboxylic acids such as maleic acid, itaconic acid, succinic acid and adipic acid, anhydrides thereof, acrylic acid, and methacrylic acid, and maleic anhydride is most preferable from the viewpoint of ease of modification, general-purpose property, and the like. From the viewpoint of the heat resistance of the exterior material for electrical storage devices, the olefin component is preferably a polypropylene-based resin, and it is most preferable that the adhesive layer 5 contains maleic anhydride-modified polypropylene.

The resin forming the adhesive layer 5 can be confirmed to contain a polyolefin backbone by an analysis method such as infrared spectroscopy, gas chromatography-mass spectrometry, and the analysis method is not particularly limited. The resin forming the adhesive layer 5 is confirmed to contain an acid-modified polyolefin, for example, when peaks derived from maleic anhydride are detected near wavenumbers of 1760 cm⁻¹ and 1780 cm⁻¹ when a maleic anhydride-modified polyolefin is measured by infrared spectroscopy. However, if the degree of acid modification is low, the peaks may be too small to be detected. In that case, the peaks can be analyzed by nuclear magnetic resonance spectroscopy.

Further, from the viewpoint of securing durability, such as heat resistance and content resistance and securing moldability, of the exterior material for electrical storage devices while reducing the thickness, the adhesive layer 5 is more preferably a cured product of a resin composition containing an acid-modified polyolefin and a curing agent. Preferred examples of the acid-modified polyolefin include those described above.

The adhesive layer 5 is preferably a cured product of a resin composition containing an acid-modified polyolefin and at least one selected from the group consisting of a compound having an isocyanate group, a compound having an oxazoline group, and a compound having an epoxy group, especially preferably a cured product of a resin composition containing an acid-modified polyolefin and at least one selected from the group consisting of a compound having an isocyanate group and a compound having an epoxy group. Preferably, the adhesive layer 5 preferably contains at least one selected from the group consisting of polyurethane, polyester and epoxy resin. More preferably, the adhesive layer 5 contains polyurethane and epoxy resin. As the polyester, for example, an ester resin produced by reaction of an epoxy group with a maleic anhydride group, or an amide ester resin produced by reaction of an oxazoline group with a maleic anhydride group is preferable. When an unreacted substance of a curing agent, such as a compound having an isocyanate group, a compound having an oxazoline group, or an epoxy resin remains in the adhesive layer 5, the presence of the unreacted substance can be confirmed by, for example, a method selected from infrared spectroscopy, Raman spectroscopy, time-of-flight secondary ion mass spectrometry (TOF-SIMS) and the like.

From the viewpoint of further improving adhesion between the barrier layer 3 and the adhesive layer 5, the adhesive layer 5 is preferably a cured product of a resin composition containing a curing agent having at least one selected from the group consisting of an oxygen atom, a heterocyclic ring, a C═N bond, and a C—O—C bond. Examples of the curing agent having a heterocyclic ring include curing agents having an oxazoline group, and curing agents having an epoxy group. Examples of the curing agent having a C═N bond include curing agents having an oxazoline group and curing agents having an isocyanate group. Examples of the curing agent having a C—O—C bond include curing agents having an oxazoline group, curing agents having an epoxy group. Whether the adhesive layer 5 is a cured product of a resin composition containing any of these curing agents can be confirmed by, for example, a method such as gas chromatography-mass spectrometry (GCMS), infrared spectroscopy (IR), time-of-flight secondary ion mass spectrometry (TOF-SIMS), or X-ray photoelectron spectroscopy (XPS).

The compound having an isocyanate group is not particularly limited, and is preferably a polyfunctional isocyanate compound from the viewpoint of effectively improving adhesion between the barrier layer 3 and the adhesive layer 5. The polyfunctional isocyanate compound is not particularly limited as long as it is a compound having two or more isocyanate groups. Specific examples of the polyfunctional isocyanate-based curing agent include pentane diisocyanate (PDI), isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), polymerized or nurated products thereof, mixtures thereof, and copolymers of these compounds with other polymers. Examples thereof include adduct forms, biuret forms, and isocyanurate forms.

The content of the compound having an isocyanate group in the adhesive layer 5 is preferably in the range of 0.1 to 50 mass %, more preferably in the range of 0.5 to 40 mass % in the resin composition forming the adhesive layer 5. This enables effective improvement of adhesion between the barrier layer 3 and the adhesive layer 5.

The compound having an oxazoline group is not particularly limited as long as it is a compound having an oxazoline backbone. Specific examples of the compound having an oxazoline group include compounds having a polystyrene main chain and compounds having an acrylic main chain. Examples of the commercially available product include EPOCROS series manufactured by Nippon Shokubai Co., Ltd.

The proportion of the compound having an oxazoline group in the adhesive layer 5 is preferably in the range of 0.1 to 50 mass %, more preferably in the range of 0.5 to 40 mass % in the resin composition forming the adhesive layer 5. This enables effective improvement of adhesion between the barrier layer 3 and the adhesive layer 5.

Examples of the compound having an epoxy group include epoxy resins. The epoxy resin is not particularly limited as long as it is a resin capable of forming a crosslinked structure by epoxy groups existing in the molecule, and a known epoxy resin can be used. The weight average molecular weight of the epoxy resin is preferably about 50 to 2,000, more preferably about 100 to 1,000, still more preferably about 200 to 800. In the first present disclosure, the weight average molecular weight of the epoxy resin is a value obtained by performing measurement by gel permeation chromatography (GPC) under the condition of using polystyrene as a standard sample.

Specific examples of the epoxy resin include glycidyl ether derivatives of trimethylolpropane, bisphenol A diglycidyl ether, modified bisphenol A diglycidyl ether, bisphenol F-type glycidyl ether, novolak glycidyl ether, glycerin polyglycidyl ether and polyglycerin polyglycidyl ether. The epoxy resins may be used alone, or may be used in combination of two or more thereof.

The proportion of the epoxy resin in the adhesive layer 5 is preferably in the range of 0.1 to 50 mass %, more preferably in the range of 0.5 to 40 mass % in the resin composition forming the adhesive layer 5. This enables effective improvement of adhesion between the barrier layer 3 and the adhesive layer 5.

The polyurethane is not particularly limited, and a known polyurethane can be used. The adhesive layer 5 may be, for example, a cured product of two-liquid curable polyurethane.

The proportion of the polyurethane in the adhesive layer 5 is preferably in the range of 0.1 to 50 mass %, more preferably in the range of 0.5 to 40 mass % in the resin composition forming the adhesive layer 5. This enables effective improvement of adhesion between the barrier layer 3 and the adhesive layer 5 in an atmosphere including a component which induces corrosion of the barrier layer, such as an electrolytic solution.

When the adhesive layer 5 is a cured product of a resin composition containing at least one selected from the group consisting of a compound having an isocyanate group, a compound having an oxazoline group and an epoxy resin, and the acid-modified polyolefin, the acid-modified polyolefin functions as a main component, and the compound having an isocyanate group, the compound having an oxazoline group, and the compound having an epoxy group each function as a curing agent.

The adhesive layer 5 may contain a modifier having a carbodiimide group.

The thickness of the adhesive layer 5 is preferably about 50 μm or less, about 40 μm or less, about 30 μm or less, about 20 μm or less, or about 5 μm or less. The thickness of the adhesive layer 5 is preferably about 0.1 μm or more, or about 0.5 μm or more. The thickness of the adhesive layer 5 is preferably in the range of about 0.1 to 50 μm, about 0.1 to 40 μm, about 0.1 to 30 μm, about 0.1 to 20 μm, about 0.1 to 5 μm, about 0.5 to 50 μm, about 0.5 to 40 μm, about 0.5 to 30 μm, about 0.5 to 20 μm, or about 0.5 to 5 μm. More specifically, the thickness is preferably about 1 to 10 μm, more preferably about 1 to 5 μm in the case of the adhesive exemplified for the adhesive agent layer 2 or a cured product of an acid-modified polyolefin with a curing agent. When any of the resins exemplified for the heat-sealable resin layer 4 is used, the thickness of the adhesive layer is preferably about 2 to 50 μm, more preferably about 10 to 40 μm. When the adhesive layer 5 is a cured product of a resin composition containing the adhesive exemplified for the adhesive agent layer 2 or an acid-modified polyolefin and a curing agent, the adhesive layer 5 can be formed by, for example, applying the resin composition and curing the resin composition by heating or the like. When the resin exemplified for the heat-sealable resin layer 4 is used, for example, extrusion molding of the heat-sealable resin layer 4 and the adhesive layer 5 can be performed.

3. Method for Manufacturing Exterior Material for Electrical Storage Devices

In the first embodiment of the present disclosure, the method for manufacturing an exterior material for electrical storage devices is not particularly limited as long as a laminate is obtained in which the layers of the exterior material for electrical storage devices according to the first embodiment are laminated. Examples thereof include a method including the step of preparing a laminate in which at least the surface coating layer 6, the base material layer 1, the barrier layer 3 and the heat-sealable resin layer 4 are laminated in this order from the outside. Specifically, the method for manufacturing an exterior material for electrical storage devices according to the first embodiment includes the step of preparing a laminate in which at least the surface coating layer 6, the base material layer 1, the barrier layer 3 and the heat-sealable resin layer 4 are laminated in this order from the outside, and the logarithmic decrement ΔE of the outer surface of the surface coating layer 6 of the laminate is 0.120 or less at 60° C. in measurement with a rigid body pendulum. The method for manufacturing an exterior material for electrical storage devices according to the second embodiment includes the step of preparing a laminate in which at least the surface coating layer 6, the base material layer 1, the barrier layer 3 and the heat-sealable resin layer 4 are laminated in this order from the outside, and the logarithmic decrement ΔE of the outer surface of the surface coating layer 6 of the laminate is 0.200 or less at 110° C. in measurement with a rigid body pendulum.

An example of the method for manufacturing the exterior material for electrical storage devices of the present disclosure is as follows. First, a laminate including the base material layer 1, the adhesive agent layer 2 and the barrier layer 3 in this order (hereinafter, the laminate may be described as a “laminate A”) is formed. Specifically, the laminate A can be formed by a dry lamination method in which an adhesive to be used for formation of the adhesive agent layer 2 is applied onto the base material layer 1 or the barrier layer 3, the surface of which is subjected to a chemical conversion treatment if necessary, using a coating method such as a gravure coating method or a roll coating method, and dried, the barrier layer 3 or the base material layer 1 is then laminated, and the adhesive agent layer 2 is cured.

Then, the heat-sealable resin layer 4 is laminated on the barrier layer 3 of the laminate A. When the heat-sealable resin layer 4 is laminated directly on the barrier layer 3, the heat-sealable resin layer 4 may be laminated onto the barrier layer 3 of the laminate A by a method such as a thermal lamination method or an extrusion lamination method. When the adhesive layer 5 is provided between the barrier layer 3 and the heat-sealable resin layer 4, mention is made of, for example, (1) a method in which the adhesive layer 5 and the heat-sealable resin layer 4 are extruded to be laminated on the barrier layer 3 of the laminate A (extrusion lamination method or tandem lamination method); (2) a method in which the adhesive layer 5 and the heat-sealable resin layer 4 are laminated to form a laminate separately, and the laminate is laminated on the barrier layer 3 of the laminate A by a thermal lamination method, or a method in which a laminate with the adhesive layer 5 laminated on the barrier layer 3 of the laminate A is formed, and laminated to the heat-sealable resin layer 4 by a thermal lamination method; (3) a method in which the melted adhesive layer 5 is poured between the barrier layer 3 of the laminate A and the heat-sealable resin layer 4 formed in a sheet shape beforehand, and simultaneously the laminate A and the heat-sealable resin layer 4 are bonded together with the adhesive layer 5 interposed therebetween (sandwich lamination); and (4) an adhesive for forming the adhesive layer 5 is applied by solution coating and dried or baked to laminate the adhesive on the barrier layer 3 of the laminate A, and the heat-sealable resin layer 4 formed in a sheet shape in advance is laminated on the adhesive layer 5.

Next, the surface coating layer 6 is laminated on a surface of the base material layer 1 on a side opposite to the barrier layer 3. The surface coating layer 6 can be formed by, for example, applying the resin composition for forming the surface coating layer 6 to the surface of the base material layer 1, and curing the resin composition. The order of the step of laminating the barrier layer 3 on a surface of the base material layer 1 and the step of laminating the surface coating layer 6 on a surface of the base material layer 1 is not particularly limited. For example, the surface coating layer 6 may be formed on a surface of the base material layer 1, followed by forming the barrier layer 3 on a surface of the base material layer 1 on a side opposite to the surface coating layer 6.

As described above, a laminate including the surface coating layer 6, the base material layer 1, the adhesive agent layer 2 provided if necessary, the barrier layer 3, the adhesive layer 5 provided if necessary, and the heat-sealable resin layer 4 in this order from the outside is formed, and the laminate may be further subjected to a heating treatment for strengthening the bondability of the adhesive agent layer 2 and the adhesive layer 5 provided if necessary. As described above, a colored layer may be provided between the base material layer 1 and the barrier layer 3.

4. Uses of Exterior Material for Electrical Storage Devices

The exterior material for electrical storage devices according to the present disclosure is used as a packaging for hermetically sealing and storing electrical storage device elements such as a positive electrode, a negative electrode, and an electrolyte. That is, in a packaging formed of the exterior material for electrical storage devices, an electrical storage device element including at least a positive electrode, a negative electrode, and an electrolyte can be stored to obtain an electrical storage device.

Specifically, an electrical storage device element including at least a positive electrode, a negative electrode, and an electrolyte is covered with the exterior material for electrical storage devices according to the present disclosure such that a flange portion (region where a heat-sealable resin layer is in contact with itself) can be formed on the periphery of the electrical storage device element while a metal terminal connected to each of the positive electrode and the negative electrode protrudes to the outside, and the heat-sealable resin layer at the flange portion is heat-sealed with itself, thereby providing an electrical storage device using the exterior material for electrical storage devices. When the electrical storage device element is stored in the packaging formed of the exterior material for electrical storage devices according to the present disclosure, the packaging is formed in such a manner that the heat-sealable resin portion of the exterior material for electrical storage devices according to the present disclosure is on the inner side (a surface contacting the electrical storage device element). The heat-sealable resin layers of two exterior materials for electrical storage devices may be superposed in such a manner as to face each other, followed by heat-sealing the peripheral edge portions of the superposed exterior materials for electrical storage devices to form a packaging. Alternatively, as in the example shown in FIG. 4 , one exterior material for electrical storage devices may be folded over itself, followed by heat-sealing the peripheral edge portions to form a packaging. When the exterior material is folded over itself, a packaging may be formed by three-side sealing with the exterior material heat-sealed at sides other than the folding side as in the example shown in FIG. 4 , or may be subjected to four-side sealing with the exterior material folded in such a manner that a flange portion can be formed. In the exterior material for electrical storage devices, a concave portion for housing an electrical storage device element may be formed by deep drawing molding or bulging molding. As in the example shown in FIG. 4 , one exterior material for electrical storage devices may be provided with a concave portion while the other exterior material for electrical storage devices is not provided a concave portion, or the other exterior material for electrical storage devices may also be provided with a concave portion.

The exterior material for electrical storage devices according to the present disclosure can be suitably used for electrical storage devices such as batteries (including condensers, capacitors and the like.). The exterior material for electrical storage devices according to the present disclosure may be used for either primary batteries or secondary batteries, and is preferably used for secondary batteries. The type of a secondary battery to which the exterior material for electrical storage devices according to the present disclosure is applied is not particularly limited, and examples thereof include lithium ion batteries, lithium ion polymer batteries, solid-state batteries, lead storage batteries, nickel-hydrogen storage batteries, nickel-cadmium storage batteries, nickel-iron storage batteries, nickel-zinc storage batteries, silver oxide-zinc storage batteries, metal-air batteries, polyvalent cation batteries, condensers and capacitors. Of these secondary batteries, preferred subjects to which the exterior material for electrical storage devices according to the present disclosure is applied include lithium ion batteries and lithium ion polymer batteries.

EXAMPLES

Hereinafter, the present disclosure will be described in detail by way of examples and comparative examples. However, the present disclosure is not limited to examples.

<Manufacturing of Exterior Material for Electrical Storage Devices According to First Embodiment> Example 1A

A stretched nylon (ONy) film (thickness: 15 μm) was prepared as a base material layer. In addition, an aluminum foil (JIS H4160: 1994A 8021 H-O (thickness: 35 μm)) was prepared as a barrier layer. Next, the barrier layer and the base material layer were laminated by a dry lamination method using an adhesive (two-liquid urethane adhesive containing a colorant) as described later, and aging treatment was then performed to prepare a laminate of base material layer/adhesive agent layer/barrier layer. Both surfaces of the aluminum foil are subjected to chemical conversion treatment. The chemical conversion treatment of the aluminum foil was performed by applying to both the surfaces of the aluminum foil a treatment liquid including a phenol resin, a chromium fluoride compound and phosphoric acid using a roll coating method in such a manner that the application amount of chromium was 10 mg/m² (dry mass), and performing baking.

Next, maleic anhydride-modified polypropylene as an adhesive layer (thickness: 20 μm) and random polypropylene as a heat-sealable resin layer (thickness: 15 μm) were co-extruded onto the barrier layer of the obtained laminate of the layers to laminate an adhesive layer and a heat-sealable resin layer on the barrier layer. Further, the following resin composition 1A was applied to the surface of the base material layer of the obtained laminate to a thickness of 3 μm, and cured under the formation conditions of an environment at a temperature of 40° C. to 100° C. and 3 days to form a matte-toned surface coating layer, so that an exterior material for electrical storage devices was obtained which included a laminate (laminated configuration A, total thickness: 91 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 15 μm), an adhesive agent layer (3 μm), a barrier layer (35 μm), an adhesive layer (20 μm) and a heat-sealable resin layer (15 μm) were laminated in this order from the outside.

Examples 2A to 5A

Except that in formation of the surface coating layer, a surface coating layer was formed using each of the following resin compositions 2A to 5A in place of the resin composition 1A, the same procedure as in Example 1A was carried out to obtain an exterior material for electrical storage devices which included a laminate (laminated configuration A, total thickness: 91 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 15 μm), an adhesive agent layer (3 μm), a barrier layer (35 μm), an adhesive layer (20 μm) and a heat-sealable resin layer (15 μm) were laminated in this order from the outside.

Example 6A

Except that a stretched nylon (ONy) film (thickness: 12 μm) was used in place of the stretched nylon (ONy) film (thickness: 15 μm) as a base material layer, the thickness of the adhesive layer was 14 μm, and the thickness of the sealable resin layer was 10 μm, the same procedure as in Example 2A was carried out to obtain an exterior material for electrical storage devices which included a laminate (laminated configuration B, total thickness: 77 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 12 μm), an adhesive agent layer (3 μm), a barrier layer (35 μm), an adhesive layer (14 μm) and a heat-sealable resin layer (10 μm) were laminated in this order from the outside.

Example 7A

Except that the thickness of the adhesive layer was 14 μm, and the thickness of the sealable resin layer was 10 μm, the same procedure as in Example 2A was carried out to obtain an exterior material for electrical storage devices which included a laminate (laminated configuration C, total thickness: 80 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 15 μm), an adhesive agent layer (3 μm), a barrier layer (35 μm), an adhesive layer (14 μm) and a heat-sealable resin layer (10 μm) were laminated in this order from the outside.

Example 8A

Except that a stretched nylon (ONy) film (thickness: 20 μm) was used in place of the stretched nylon (ONy) film (thickness: 15 μm) as a base material layer, an aluminum foil (JIS H4160:1994 A8021H-O (thickness: 30 μm)) was used in place of the aluminum foil (JIS H4160:1994 A8021H-O (thickness: 35 μm)), the thickness of the adhesive layer was 14 μm, and the thickness of the sealable resin layer was 10 μm, the same procedure as in Example 2A was carried out to obtain an exterior material for electrical storage devices which included a laminate (laminated configuration D, total thickness: 80 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 20 μm), an adhesive agent layer (3 μm), a barrier layer (30 μm), an adhesive layer (14 μm) and a heat-sealable resin layer (10 μm) were laminated in this order from the outside.

Example 9A

Except that a stretched nylon (ONy) film (thickness: 20 μm) was used in place of the stretched nylon (ONy) film (thickness: 15 μm) as a base material layer, the thickness of the adhesive layer was 15 μm, and the thickness of the sealable resin layer was 15 μm, the same procedure as in Example 2A was carried out to obtain an exterior material for electrical storage devices which included a laminate (laminated configuration E, total thickness: 91 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 20 μm), an adhesive agent layer (3 μm), a barrier layer (35 μm), an adhesive layer (15 μm) and a heat-sealable resin layer (15 μm) were laminated in this order from the outside.

Example 10A

Except that an aluminum foil (JIS H4160:1994 A8021H-O (thickness: 40 μm)) was used in place of the aluminum foil (JIS H4160:1994 A8021H-O (thickness: 35 μm)), the thickness of the adhesive layer was 15 μm, and the thickness of the sealable resin layer was 15 μm, the same procedure as in Example 2A was carried out to obtain an exterior material for electrical storage devices which included a laminate (laminated configuration F, total thickness: 91 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 15 μm), an adhesive agent layer (3 μm), a barrier layer (40 μm), an adhesive layer (15 μm) and a heat-sealable resin layer (15 μm) were laminated in this order from the outside.

Example 11A

A stretched nylon (ONy) film (thickness: 12 μm) was prepared as a base material layer. A stainless steel foil (SUS 304 (thickness: 20 μm)) was provided as a barrier layer. Next, the barrier layer and the base material layer were laminated by a dry lamination method using an adhesive (two-liquid urethane adhesive containing a colorant) as described later, and aging treatment was then performed to prepare a laminate of base material layer/adhesive agent layer/barrier layer. Both surfaces of the stainless steel foil are subjected to chemical conversion treatment. The chemical conversion treatment of the stainless steel foil was performed by applying to both the surfaces of the stainless steel foil a treatment liquid including a phenol resin, a chromium fluoride compound and phosphoric acid using a roll coating method in such a manner that the application amount of chromium was 10 mg/m² (dry mass), and performing baking.

Next, the barrier layer and the heat-sealable resin layer of each laminate obtained as described above were bonded to each other by a dry lamination method with a modified olefin-based adhesive (the thickness of the cured adhesive layer is 3 μm) to laminate the adhesive layer and the heat-sealable resin layer on the barrier layer. As the heat-sealable resin layer, an unstretched polypropylene film (thickness: 20 μm) was used. Further, the following resin composition 1A was applied to the surface of the base material layer of the obtained laminate to a thickness of 3 μm, and cured under the formation conditions of an environment at a temperature of 40° C. to 100° C. and 3 days to form a matte-toned surface coating layer, so that an exterior material for electrical storage devices was obtained which included a laminate (laminated configuration G, total thickness: 61 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 12 μm), an adhesive agent layer (3 μm), a barrier layer (20 μm), an adhesive layer (3 μm) and a heat-sealable resin layer (20 μm) were laminated in this order from the outside.

Comparative Example 1A

Except that in formation of the surface coating layer, a surface coating layer was formed using the following resin composition 6A in place of the resin composition 1A, the same procedure as in Example 1A was carried out to obtain an exterior material for electrical storage devices which included a laminate (laminated configuration A, total thickness: 91 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 15 μm), an adhesive agent layer (3 μm), a barrier layer (35 μm), an adhesive layer (20 μm) and a heat-sealable resin layer (15 μm) were laminated in this order from the outside.

<Resin Composition Used for Formation of Surface Coating Layer and Formation Conditions>

(Resin Composition 1A (Used in Examples 1A and 11A))

Resin composition containing a resin (polyurethane formed from a mixture of an acryl-based polyol compound and an aliphatic isocyanate-based compound), an inorganic filler (silica particles having an average particle diameter of 1 μm), an organic filler (average particle diameter: 2 μm), and an olefin-based wax.

(Resin Composition 2A (Used in Examples 2A and 6A to 10A))

Resin composition containing a resin (polyurethane formed from a mixture of an acryl-based polyol compound, an aromatic isocyanate-based compound and a urethane resin), an inorganic filler (silica particles having an average particle diameter of 1 μm), and an organic filler (average particle diameter: 2 μm).

(Resin Composition 3A (Used in Example 3A))

A resin composition similar to the resin composition 2A except that the aromatic isocyanate-based compound used in the resin composition 2A is used in an amount ½ the amount of that used in the resin composition 2A.

(Resin Composition 4A (Used in Example 4A))

A resin composition similar to the resin composition 2A except that the aromatic isocyanate-based compound used in the resin composition 2A is used in an amount ¼ the amount of that used in the resin composition 2A.

(Resin Composition 5A (Used in Example 5A))

A resin composition similar to the resin composition 2A except that the aromatic isocyanate-based compound used in the resin composition 2A is used in an amount 1/10 the amount of that used in the resin composition 2A.

(Resin Composition 6A (Used in Comparative Example 1A))

Except that an aliphatic isocyanate-based compound different from that of the resin composition 1A used in Example 1A was used, the same material as that of the resin composition 1A used in Example 1A was used.

[Measurement of Logarithmic Decrement ΔE of Outer Surface of Surface Coating Layer]

The exterior material for electrical storage devices was cut into a rectangle having a width of 15 mm (TD: Transverse Direction) and a length of 100 mm (MD: Machine Direction). Next, the adhesive layer and the heat-sealable resin layer were peeled from the barrier layer. Specifically, at 20 mm from the end in the length direction, a cut was made which extends from the surface coating layer side to the barrier layer. Pulling was performed from the left and the right with the cut at the center, so that the cut in the surface coating layer and the barrier layer was expanded to achieve cutting, and the adhesive layer and the heat-sealable resin layer were stretched. At the time when the adhesive layer and the heat-sealable resin layer were stretched, the adhesive layer and the heat-sealable resin layer were peeled from the barrier layer. The exterior material for electrical storage devices in which the adhesive layer and the heat-sealable resin layer are peeled is cut into a rectangle having a width of 15 mm (TD) and a length of 50 mm (MD: Machine Direction) to obtain a test sample S. Next, as shown in FIG. 5 , a rigid body pendulum physical property tester (model: RPT-3000W manufactured by A&D Company, Limited) was used, FRB-100 was used for a frame of a pendulum 30, cylindrical cylinder edge 30 a (RBP-080) was used for the edge portion, and the initial amplitude was set to about 0.3 degrees. The pendulum 30 was placed in such a manner that the central axis direction of the cylindrical cylinder and the machine direction of the test sample S were orthogonal to each other. For preventing floating and warpage of the test sample S during measurement, a kapton tape was attached to the test sample S at a position having no effect on measurement results, and fixed. The cylindrical cylinder edge 30 a was brought into contact with the outer surface of the surface coating layer. Next, the logarithmic decrement ΔE of the surface coating layer was measured in a temperature range of 30° C. to 200° C. at a temperature rise rate of 3° C./min using a cold block 31 (CHB-100). A logarithmic decrement ΔE at which the temperature of the surface coating layer of the test sample S was 30° C. and a logarithmic decrement ΔE at which the temperature of the surface coating layer of the test sample S was 60° C. were adopted. An average of two measurements (N=2) made by using an unused cut sample rather than using a test sample once measured was used.

[Evaluation of Tape Adhesion]

Adhesion of the pressure sensitive adhesive tape to the outer surface of the surface coating layer of the exterior material for electrical storage devices was evaluated by the following procedure. This will be described with reference to FIGS. 6 and 7 . The exterior material 10 for electrical storage devices was cut into a rectangular shape of 60 mm in length (MD) and 50 mm in width (TD). As shown in the schematic diagrams of FIGS. 6 and 7 , a double-sided pressure sensitive adhesive tape 41 (60 mm in length and 50 mm in width) was bonded to one surface of an acrylic plate 40 (2 mm in thickness, 75 mm in length and 50 mm in width), and the heat-sealable resin layer 4 of the cut exterior material 10 for electrical storage devices was bonded to the double-sided pressure sensitive adhesive tape 41. On the other hand, two aluminum foils 43 (one surface is glossy and the other surface is not glossy; 35 μm in thickness, 150 mm in length and 15 mm in width) and the double-sided pressure sensitive adhesive tape 42 (containing an acryl-based pressure sensitive adhesive as a pressure sensitive adhesive; 50 mm in length and 12.5 mm in width) were provided, and the glossy surface of the aluminum foil 43 and one surface of the double-sided pressure sensitive adhesive tape 42 were bonded to each other. Next, one surface of the double-sided pressure sensitive adhesive tape 42 which had been bonded to the aluminum foil 43 and the outer surface of the surface coating layer 6 of the exterior material 10 for electrical storage devices which had been bonded to the acrylic plate were lightly attached to each other. Further, by reciprocating a roller (2 kg) once from the aluminum foil 43 side, the double-sided pressure sensitive adhesive tape 42 and the outer surface of the surface coating layer 6 of the exterior material 10 for electrical storage devices were brought into close contact with each other, and left standing at room temperature (25° C.) for 1 hour to obtain a test sample. Next, in an environment at 60° C. or an environment at 30° C., a portion of the acrylic plate 40 to which the double-sided pressure sensitive adhesive tape 41 was not bonded and an end part of the aluminum foil 43 to which the double-sided pressure sensitive adhesive tape 42 was not bonded were each chucked, pulling was performed in a 180° direction, and an average value of strokes of 20 mm to 80 mm was determined to evaluate tape adhesion. As a tensile tester, trade name ΔG-Xplus manufactured by Shimadzu Corporation was used, and measurement conditions were set to a tensile speed of 300 mm/min and a stroke of 90 mm. As a value for evaluation of tape adhesion, an average of two measurements (N=2) was used. The results are shown in Table 1A.

TABLE 1A Surface coating layer Laminated configuration Logarithmic Logarithmic Tape adhesion Tape adhesion of exterior material for decrement ΔE decrement ΔE at 60° C. at 30° C. electrical storage devices at 60° C. at 30° C. (N/15 mm) (N/15 mm) Example 1A A 0.058 0.045 9.6 19.0 Example 2A A 0.070 0.050 9.4 20.0 Example 3A A 0.055 0.045 9.3 20.0 Example 4A A 0.078 0.050 8.8 18.7 Example 5A A 0.081 0.047 8.1 17.2 Example 6A B 0.081 0.047 9.4 20.0 Example 7A C 0.081 0.047 9.4 20.0 Example 8A D 0.081 0.047 9.4 20.0 Example 9A E 0.081 0.047 9.4 20.0 Example 10A F 0.081 0.047 9.4 20.0 Example 11A G 0.048 0.041 9.4 20.0 Comparative A 0.126 0.094 4.5 20.0 Example 1A

Comparative Example 1A is an exterior material for electrical storage devices which includes a conventional standard surface coating layer, and the logarithmic decrement ΔE of the outer surface of the surface coating layer at 60° C. in measurement with a rigid body pendulum exceeds 0.12. On the other hand, in the exterior material for electrical storage devices in each of Examples 1A to 11A, the logarithmic decrement ΔE of the outer surface of the surface coating layer at 60° C. in measurement with a rigid body pendulum is 0.12 or less. It can be seen that in the exterior material for electrical storage devices in Example 1A to 11A, not only tape adhesion at 30° C. but also tape adhesion in a high-temperature environment at 60° C. is high.

As described above, the first embodiment of the present disclosure provides the invention of aspects as shown below.

Item 1A. An exterior material for electrical storage devices including a laminate including at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in this order from the outside, in which a logarithmic decrement ΔE of an outer surface of the surface coating layer of the laminate is 0.120 or less at 60° C. in measurement with a rigid body pendulum. Item 2A. The exterior material for electrical storage devices according to item 1A, in which the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate at 30° C. in measurement with a rigid body pendulum is 0.080 or less. Item 3A. The exterior material for electrical storage devices according to item 1A to 2A, including an adhesive agent layer between the base material layer and the barrier layer. Item 4A. The exterior material for electrical storage devices according to item 3A, in which the adhesive agent layer is colored. Item 5A. The exterior material for electrical storage devices according to any one of items 1A to 4A, including a colored layer between the base material layer and the barrier layer. Item 6A. The exterior material for electrical storage devices according to any one of items 1A to 5A, in which the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate at 60° C. in measurement with a rigid body pendulum is 0.060 or more. Item 7A. A method for manufacturing an exterior material for electrical storage devices, the method comprising the step of preparing a laminate in which at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer are laminated in this order from the outside, in which

a logarithmic decrement ΔE of an outer surface of the surface coating layer of the laminate is 0.120 or less at 60° C. in measurement with a rigid body pendulum.

Item 8A. An electrical storage device in which an electrical storage device element including at least a positive electrode, a negative electrode, and an electrolyte is stored in a packaging formed of the exterior material for electrical storage devices according to any one of items 1A to 6A.

<Manufacturing of Exterior Material for Electrical Storage Devices According to Second Embodiment> Example 1B

A stretched nylon (ONy) film (thickness: 12 μm) was prepared as a base material layer. A stainless steel foil (SUS 304 (thickness: 20 μm)) was provided as a barrier layer. Next, the barrier layer and the base material layer were laminated by a dry lamination method using an adhesive (two-liquid urethane adhesive containing a colorant) as described later, and aging treatment was then performed to prepare a laminate of base material layer/adhesive agent layer/barrier layer. Both surfaces of the stainless steel foil are subjected to chemical conversion treatment. The chemical conversion treatment of the stainless steel foil was performed by applying to both the surfaces of the stainless steel foil a treatment liquid including a phenol resin, a chromium fluoride compound and phosphoric acid using a roll coating method in such a manner that the application amount of chromium was 10 mg/m² (dry mass), and performing baking.

Next, the barrier layer and the heat-sealable resin layer of each laminate obtained as described above were bonded to each other by a dry lamination method with a modified olefin-based adhesive (the thickness of the cured adhesive layer is 3 μm) to laminate the adhesive layer and the heat-sealable resin layer on the barrier layer. As the heat-sealable resin layer, an unstretched polypropylene film (thickness: 20 μm) was used. Further, the following resin composition 1B was applied to the surface of the base material layer of the obtained laminate to a thickness of 3 μm, and cured under the formation conditions of an environment at a temperature of 40° C. to 100° C. and 3 days to form a matte-toned surface coating layer, so that an exterior material for electrical storage devices was obtained which included a laminate (total thickness: 61 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 12 μm), an adhesive agent layer (3 μm), a barrier layer (20 μm), an adhesive layer (3 μm) and a heat-sealable resin layer (20 μm) were laminated in this order from the outside.

Example 2B

A stretched nylon (ONy) film (thickness: 15 μm) was prepared as a base material layer. In addition, an aluminum foil (JIS H4160: 1994A 8021 H-O (thickness: 35 μm)) was prepared as a barrier layer. Next, the barrier layer and the base material layer were laminated by a dry lamination method using an adhesive (two-liquid urethane adhesive containing a colorant) as described later, and aging treatment was then performed to prepare a laminate of base material layer/adhesive agent layer/barrier layer. Both surfaces of the aluminum foil are subjected to chemical conversion treatment. The chemical conversion treatment of the aluminum foil was performed by applying to both the surfaces of the aluminum foil a treatment liquid including a phenol resin, a chromium fluoride compound and phosphoric acid using a roll coating method in such a manner that the application amount of chromium was 10 mg/m² (dry mass), and performing baking.

Next, maleic anhydride-modified polypropylene as an adhesive layer (thickness: 20 μm) and random polypropylene as a heat-sealable resin layer (thickness: 20 μm) were co-extruded onto the barrier layer of the obtained laminate of the layers to laminate an adhesive layer and a heat-sealable resin layer on the barrier layer. Further, the following resin composition 2B was applied to the surface of the base material layer of the obtained laminate to a thickness of 3 μm, and cured under the formation conditions of an environment at a temperature of 40° C. to 100° C. and 3 days to form a matte-toned surface coating layer, so that an exterior material for electrical storage devices was obtained which included a laminate (total thickness: 91 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 15 μm), an adhesive agent layer (3 μm), a barrier layer (35 μm), an adhesive layer (20 μm) and a heat-sealable resin layer (20 μm) were laminated in this order from the outside.

Example 3B

Except that for formation of the surface coating layer, the resin composition 2B was used in place of the resin composition 1B, the same procedure as in Example 1B was carried out to obtain an exterior material for electrical storage devices which included a laminate (total thickness: 61 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 12 μm), an adhesive agent layer (3 μm), a barrier layer (20 μm), an adhesive layer (3 μm) and a heat-sealable resin layer (20 μm) were laminated in this order from the outside.

Example 4B

Except that for formation of the surface coating layer, a resin composition 3B was used in place of the resin composition 1B, the same procedure as in Example 1B was carried out to obtain an exterior material for electrical storage devices which included a laminate (total thickness: 61 μm) in which a surface coating layer (3 μm), a base material layer (thickness: 12 μm), an adhesive agent layer (3 μm), a barrier layer (20 μm), an adhesive layer (3 μm) and a heat-sealable resin layer (20 μm) were laminated in this order from the outside.

Comparative Example 1B

Except that in place of the resin composition 2B, the following resin composition 1B was used to form a surface coating layer in formation of the surface coating layer, the same procedure as in Example 2B was carried out to obtain an exterior material for electrical storage devices.

<Resin Composition Used for Formation of Surface Coating Layer and Formation Conditions>

(Resin Composition 1B (Used in Example 1B and Comparative Example 1B))

Resin composition containing a resin (polyurethane formed from a mixture of an acryl-based polyol compound, an aliphatic isocyanate-based compound and a urethane resin), an inorganic filler (silica particles having an average particle diameter of 1 μm), and an organic filler (average particle diameter: 2 μm).

(Resin Composition 2B (Used in Example 2B and Example 3B))

Resin composition containing a resin (polyurethane formed from a mixture of an acryl-based polyol compound, an aromatic isocyanate-based compound and a urethane resin), an inorganic filler (silica particles having an average particle diameter of 1 μm), and an organic filler (average particle diameter: 2 μm).

(Resin Composition 3B (Used in Example 4B))

Resin composition containing a resin (polyurethane formed from a mixture of an acryl-based polyol compound, an aromatic isocyanate-based compound and a urethane resin) and an inorganic filler (silica particles having an average particle diameter of 1 μm) (identical to the resin composition 2B except that there is no organic filler)

[Measurement of Logarithmic Decrement ΔE of Outer Surface of Surface Coating Layer]

The exterior material for electrical storage devices was cut into a rectangle having a width of 15 mm (TD: Transverse Direction) and a length of 100 mm (MD: Machine Direction). Next, the adhesive layer and the heat-sealable resin layer were peeled from the barrier layer. Specifically, at 20 mm from the end in the length direction, a cut was made which extends from the surface coating layer side to the barrier layer. Pulling was performed from the left and the right with the cut at the center, so that the cut in the surface coating layer and the barrier layer was expanded to achieve cutting, and the adhesive layer and the heat-sealable resin layer were stretched. At the time when the adhesive layer and the heat-sealable resin layer were stretched, the adhesive layer and the heat-sealable resin layer were peeled from the barrier layer. The exterior material for electrical storage devices in which the adhesive layer and the heat-sealable resin layer are peeled is cut into a rectangle having a width of 15 mm (TD) and a length of 50 mm (MD: Machine Direction) to obtain a test sample S. Next, as shown in FIG. 5 , a rigid body pendulum physical property tester (model: RPT-3000W manufactured by A&D Company, Limited) was used, FRB-100 was used for a frame of a pendulum 30, cylindrical cylinder edge 30 a (RBP-080) was used for the edge portion, and the initial amplitude was set to about 0.3 degrees. The pendulum 30 was placed in such a manner that the central axis direction of the cylindrical cylinder and the machine direction of the test sample S were orthogonal to each other. For preventing floating and warpage of the test sample S during measurement, a kapton tape was attached to the test sample S at a position having no effect on measurement results, and fixed. The cylindrical cylinder edge 30 a was brought into contact with the outer surface of the surface coating layer. Next, the logarithmic decrement ΔE of the surface coating layer was measured in a temperature range of 30° C. to 200° C. at a temperature rise rate of 3° C./min using a cold block 31 (CHB-100). A logarithmic decrement ΔE at which the temperature of the surface coating layer of the test sample S was 30° C. and a logarithmic decrement ΔE at which the temperature of the surface coating layer of the test sample S was 110° C. were adopted. An average of two measurements (N=2) made by using an unused cut sample S rather than using the test sample S once measured was used.

[Evaluation of Damage Resistance at 110° C.]

A test piece was obtained by cutting the exterior material for electrical storage devices into a rectangle having a width of 30 mm (TD: Transverse Direction) and a length of 100 mm (MD: Machine Direction). Next, the test piece was placed on a flat glass plate of 150 mm square with the surface coating layer being on the upper side, and the end part of the test piece was fixed with a tape so that the heat-sealable resin layer was in close contact with the glass plate. In this state, the test piece was left standing in an oven at 110° C. for 10 minutes. Next, the test piece was taken out from the oven, and the subsequent steps were immediately performed. A ruler was put on the surface coating layer of the test piece, and the surface of the surface coating layer was scratched with each of pencils having a pointed tip (pencils with core hardness grades 4B, B and 2H, respectively, were used). Next, the test piece was removed from the glass plate, a surface on the heat-sealable resin layer side was observed, and the damage resistance of the exterior material for electrical storage devices at 110° C. on the basis of the following criteria. The results are shown in Table 1.

A: Either a convex shape or a clear streak is not observed on the heat-sealable resin layer. B: A slight convex shape is observed on the heat-sealable resin layer side, and a clear streak is not observed. C: A large convex shape and a clear streak are observed on the heat-sealable resin layer.

[Evaluation of Damage Resistance at 30° C.]

A test piece was obtained by cutting the exterior material for electrical storage devices into a rectangle having a width of 30 mm (TD: Transverse Direction) and a length of 100 mm (MD: Machine Direction). Next, the test piece was placed on a flat glass plate of 150 mm square with the surface coating layer being on the upper side, and the end part of the test piece was fixed with a tape so that the heat-sealable resin layer was in close contact with the glass plate. In this state, the test piece was placed in an environment at 30° C., a ruler was put on the surface coating layer of the test piece, and the surface of the surface coating layer was scratched with each of pencils having a pointed tip (pencils with core hardness grades 4B, B and 2H, respectively, were used). Next, the test piece was removed from the glass plate, a surface on the heat-sealable resin layer side was observed, and the damage resistance of the exterior material for electrical storage devices at 110° C. on the basis of the following criteria. The results are shown in Table 1.

A: Either a convex shape or a clear streak is not observed on the heat-sealable resin layer. B: A slight convex shape is observed on the heat-sealable resin layer side, and a clear streak is not observed. C: A large convex shape and a clear streak are observed on the heat-sealable resin layer.

TABLE 1B Evaluation Evaluation of damage of damage Surface coating layer resistance resistance Logarithmic Logarithmic at 110° C. at 30° C. decrement decrement Pencil core Pencil core ΔE at ΔE at hardness hardness 110° C. 30° C. 4B B 2H 4B B 2H Example 1B 0.150 0.041 A A A A A A Example 2B 0.141 0.051 A B C A B C Example 3B 0.120 0.047 A A A A A A Example 4B 0.100 0.043 A A A A A A Comparative 0.220 0.045 A C C A B C Example 1B

In the exterior material for electrical storage devices in each of Examples 1B to 4B, the logarithmic decrement ΔE of the outer surface of the surface coating layer at 110° C. in measurement with a rigid body pendulum is 0.200 or less. The exterior material for electrical storage devices in each of Examples 1B to 4B was confirmed to be hardly damaged as either a large convex shape or a clear streak was not observed on the heat-sealable resin layer side in a high-temperature environment at 110° C. when a pencil with core hardness grade B which is harder than that with core hardness grade 4B was used. In particular, the exterior material for electrical storage devices in each of Examples 1B, 3B and 4B was confirmed to be hardly damaged as either a large convex shape or a clear streak was not observed on the heat-sealable resin layer side even when a very hard pencil with core hardness grade 2H was used in a high-temperature environment at 110° C.

As described above, the second embodiment of the present disclosure provides the invention of aspects as shown below.

Item 1B. An exterior material for electrical storage devices including a laminate including at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in this order from the outside, in which a logarithmic decrement ΔE of an outer surface of the surface coating layer of the laminate is 0.200 or less at 110° C. in measurement with a rigid body pendulum. Item 2B. The exterior material for electrical storage devices according to item 1B, in which the barrier layer contains a stainless steel foil. Item 3B. The exterior material for electrical storage devices according to item 1B or 2B, in which the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate at 30° C. in measurement with a rigid body pendulum is 0.080 or less. Item 4B. The exterior material for electrical storage devices according to any one of items 1B to 3B, in which the surface coating layer contains a resin and a filler. Item 5B. The exterior material for electrical storage devices according to any one of items 1B to 4B, including an adhesive agent layer between the base material layer and the barrier layer. Item 6B. The exterior material for electrical storage devices according to any one of items 1B to 5B, in which the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate at 110° C. in measurement with a rigid body pendulum is 0.145 or less. Item 7B. The exterior material for electrical storage devices according to any one of items 1B to 6B, further including an adhesive layer between the barrier layer and the heat-sealable resin layer. Item 8B. A method for manufacturing an exterior material for electrical storage devices, the method comprising the step of preparing a laminate in which at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer are laminated in this order from the outside, in which a logarithmic decrement ΔE of an outer surface of the surface coating layer of the laminate is 0.200 or less at 110° C. in measurement with a rigid body pendulum. Item 9B. An electrical storage device in which an electrical storage device element including at least a positive electrode, a negative electrode, and an electrolyte is stored in a packaging formed of the exterior material for electrical storage devices according to any one of items 1B to 7B.

DESCRIPTION OF REFERENCE SIGNS

-   -   1: Base material layer     -   2: Adhesive agent layer     -   3: Barrier layer     -   4: Heat-sealable resin layer     -   5: Adhesive layer     -   6: Surface coating layer     -   10: Exterior material for electrical storage devices     -   30: Pendulum     -   30 a: Cylindrical cylinder edge     -   31: Cold block     -   32: Vibration displacement detector     -   33: Weight     -   40: Acrylic plate     -   41: Double-sided pressure sensitive adhesive tape     -   42: Double-sided pressure sensitive adhesive tape     -   43: Aluminum foil     -   S: Test sample 

1. An exterior material for electrical storage devices comprising a laminate including at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in this order from the outside, wherein a logarithmic decrement ΔE of an outer surface of the surface coating layer of the laminate is 0.120 or less at 60° C. in measurement with a rigid body pendulum.
 2. The exterior material for electrical storage devices according to claim 1, wherein the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate at 60° C. in measurement with a rigid body pendulum is 0.060 or more.
 3. An exterior material for electrical storage devices comprising a laminate including at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer in this order from the outside, wherein a logarithmic decrement ΔE of an outer surface of the surface coating layer of the laminate is 0.200 or less at 110° C. in measurement with a rigid body pendulum.
 4. The exterior material for electrical storage devices according to claim 3, wherein the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate at 110° C. in measurement with a rigid body pendulum is 0.145 or less.
 5. The exterior material for electrical storage devices according to claim 1, wherein the logarithmic decrement ΔE of the outer surface of the surface coating layer of the laminate at 30° C. in measurement with a rigid body pendulum is 0.080 or less.
 6. The exterior material for electrical storage devices according to claim 1, comprising an adhesive agent layer between the base material layer and the barrier layer.
 7. The exterior material for electrical storage devices according to claim 6, wherein the adhesive agent layer is colored.
 8. The exterior material for electrical storage devices according to claim 1, comprising a colored layer between the base material layer and the barrier layer.
 9. The exterior material for electrical storage devices according to claim 1, wherein the barrier layer contains at least one of an aluminum alloy foil and a stainless steel foil.
 10. The exterior material for electrical storage devices according to claim 1, wherein the surface coating layer contains a resin and a filler.
 11. The exterior material for electrical storage devices according to claim 1, further comprising an adhesive layer between the barrier layer and the heat-sealable resin layer.
 12. A method for manufacturing an exterior material for electrical storage devices, the method comprising the step of preparing a laminate in which at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer are laminated in this order from the outside, wherein a logarithmic decrement ΔE of an outer surface of the surface coating layer of the laminate is 0.120 or less at 60° C. in measurement with a rigid body pendulum.
 13. A method for manufacturing an exterior material for electrical storage devices, the method comprising the step of preparing a laminate in which at least a surface coating layer, a base material layer, a barrier layer, and a heat-sealable resin layer are laminated in this order from the outside, wherein a logarithmic decrement ΔE of an outer surface of the surface coating layer of the laminate is 0.200 or less at 110° C. in measurement with a rigid body pendulum.
 14. An electrical storage device in which an electrical storage device element comprising at least a positive electrode, a negative electrode, and an electrolyte is stored in a packaging formed of the exterior material for electrical storage devices according to claim
 1. 15. The exterior material for electrical storage devices according to claim 10, wherein the filler is silica.
 16. The exterior material for electrical storage devices according to claim 1, wherein the surface coating layer is formed of polyurethane comprising a polyol compound and an aromatic isocyanate compound.
 17. The exterior material for electrical storage devices according to claim 1, wherein two or more slipping agents are present on at least one of the surface and the interior of the surface coating layer.
 18. The exterior material for electrical storage devices according to claim 1, wherein at least two selected from the group consisting of the amide-based slipping agent include saturated fatty acid amides, unsaturated fatty acid amides, substituted amides, methylol amides, saturated fatty acid bisamides, unsaturated fatty acid bisamides, fatty acid ester amides, and aromatic bisamides are present on at least one of the surface and the interior of the surface coating layer.
 19. The exterior material for electrical storage devices according to claim 1, wherein the thickness of the barrier layer is 200 μm or less, and the thickness of the barrier layer is 50 μm or less, or alternatively, the thickness of the barrier layer is more than 50 μm and 200 μm or less.
 20. The exterior material for electrical storage devices according to claim 1, wherein the heat-sealable resin layer is composed of two or more layers with the same resin component or different resin components.
 21. The exterior material for electrical storage devices according to claim 1, wherein two or more slipping agents are present on at least one of the surface and the interior of the heat-sealable resin layer.
 22. The exterior material for electrical storage devices according to claim 1, wherein at least two selected from the group consisting of the amide-based slipping agent include saturated fatty acid amides, unsaturated fatty acid amides, substituted amides, methylol amides, saturated fatty acid bisamides, unsaturated fatty acid bisamides, fatty acid ester amides, and aromatic bisamides are present on at least one of the surface and the interior of the heat-sealable resin layer.
 23. The method according to claim 12, wherein an adhesive layer is provided between the barrier layer and the heat-sealable resin layer, and the adhesive layer and the heat-sealable resin layer are formed by a coextrusion lamination method, a tandem lamination method, a thermal lamination method, a sandwich lamination method, or an adhesive for forming the adhesive layer is applied on the barrier layer, and the heat-sealable resin layer formed in a sheet shape in advance is laminated on the adhesive layer.
 24. The method according to claim 23, wherein the heat-sealable resin layer is composed of two or more layers with the same resin component or different resin components. 